Besco, Stefano (2009) Ottimizzazione formulativa e di processo nella sintesi di tecnopolimeri nanocompositi. [Tesi di dottorato]

Full text disponibile come:

[img]Documento PDF
Tesi non accessible per motivi correlati alla proprietà intellettuale.
Visibile a: nessuno

38Mb

Abstract (inglese)

The field of nanotechnology is one of the most popular areas for current research and development in a large number os technical disciplines. These obviously include polymer science and technology and even in this field the investigations cover a broad range of topics.
The studies presented in this dissertation are focused on some specific aspects resulting from researches involving several years in the field of polymer based nanocomposites, in particuar, dealing with the effects of processing techniques and conditions on the structure and properties of composite materials as well as with the consequences of the partial thermal degradation of nanostructured additives during the manufacturing process (melt blending) and the behavior of these ones when they are blended in multiphase polymer matrices.
Four different kinds of engineered polymers have been choosen, with increasing complexity dealing with their structure and morphology: an homopolimer (polyamide 66, PA66), a copolymer (acrylonitrile-butadiene-styrene, ABS) and two polymer blends characterised by phase separation in their structure (polycarbonate/ABS and PA66/polyamide 12).
They all belong to the group of the so called engineered polymers, which are polymers that can conjugatedifferent and often anthitetical properties to be used in hi-tech applications. The high costs of these enginereed polymers justifies the use of nanostructured additives, that strongly influences the final cost of composite materials.
The work discussed in this dissertation allows the comprension, for the specifific cases studied, of the role of clay’s surfactants in the dispersion process as well as of the relationships existing between nanocomposite’s structure and process parameters allowing the dispersion of nanodimensional structures also if severe thermal and mechanical stress conditions are present. The efficiency and potential of low temperature solution intercalation processes and innovative additives characterised by high thermal stability properties have also been investigated and proved. An innovative technique for morphological characterisation, based on laser induced fluorescence (LIF) of optical probes, has been purposed, applied and its correctness has been confirmed by comparison with the results of traditional characterisation techniques (TEM, SEM). Moreover LIF can be applied on larger scale in the industrial manufacturing and testing of organically modified layered silicates.
Very complex systems, in terms of structure and morphology of the multiphase polymer matrix, have been studyed and considered in order to investigate and understand the compatibilising effect of nanostructured additives in phase separated blends and the interactions between different kinds of additives when mixed togheter(organically modified layered silicates and carbon nanotubes). A semi empirical model, based on the classic models often used to describe and predict polymer composites properties, has been purposed in order to estimate the exfoliation ratio of polymer based nanocomposites from mechanical characterisation and X-ray diffraction data only.

Abstract (italiano)

Le nanotecnologie applicate alla scienza e tecnologia dei materiali polimerici rappresentano attualmente un’area di assoluto interesse e fermento per la ricerca e lo sviluppo di base ed applicati. Il lavoro svolto e discusso in questa tesi mira ad approfondire alcune criticità emerse da anni di studi effettuati nel campo dei nanocompositi a matrice polimerica, in particolare relativamente agli effetti del tipo di processo di dispersione adottato e dei parametri operativi scelti nonchè le ripercussioni della parziale degradazione degli additivi nanostrutturati durante la preparazione dei compositi ed il comportamento degli stessi quando additivati matrici polimeriche particolarmente complesse.
Sono state innanzitutto individuate quattro tipologie di tecnopolimeri a complessità crescente dal punto di vista della struttura e della morfologia: un omopolimero (poliammide 66, PA66), un copolimero (acrilonitrile-butadiene stirene (ABS) e due miscele polimeriche a separazione di fase (miscela policarbonato/ABS e PA66/poliammide 12). Tutte afferiscono alla categoria dei cosiddetti tecnopolimeri, ovvero materiali polimerici particolarmente interessanti dal punto di vista del connubio fra diverse proprietà, spesso antitetiche, che li caratterizzano e, per questo, spesso impiegati in applicazioni ad elevato contenuto tecnologico. A livello applicativo l’elevato costo dei tecnopolimeri nonché il notevole valore aggiunto dei sistemi nei quali vengono impiegati giustifica l’impiego di additivi nanostrutturati, che indubbiamente influiscono sul costo finale dei materiali ottenuti.
Il lavoro svolto ha permesso di chiarire, nei casi specifici trattati, il reale ruolo degli additivi compatibilizzanti nel processo di dispersione dei silicati lamellari organomodificati in matrici polimeriche nonché le correlazioni fra la struttura dei compositi ottenuti ed i parametri di processo che, se correttamente impostati, consentono di ottenere dispersioni nanometriche anche in condizioni di stress termico particolarmente gravose. Si sono valutate le potenzialità e l’efficienza di processi produttivi alternativi al melt blending e di additivi modificati con compatibilizzanti sperimentali dalle notevoli caratteristiche di stabilità termica alle alte temperature.
E’ stato inoltre proposta, applicata e validata con interessanti risultati una tecnica di caratterizzazione innovativa che si basa sulla fluorescenza indotta da laser (LIF) di opportune sonde ottiche, facilmente trasferibile su larga scala nella produzione industriale di additivi.
Sono stati considerati e studiati sistemi particolarmente complessi al fine di comprendere l’effetto degli additivi nanostrutturati nella compatibilizzazione delle miscele polimeriche a separazione di fase e le interazioni fra diverse tipologie di additivi (nello specifico silicati lamellari e nanotubi in carbonio) dispersi in miscele polimeriche complesse.
E’ stato infine proposto un modello che, basandosi sui classici modelli predittivi sviluppati per i compositi polimerici, permette, a partire da dati di caratterizzazione fisico meccanica e diffrattometrica, di stimare il grado di esfoliazione in un nanocomposito polimerico contenente silicati lamellari organomodificati.

Aggiungi a RefWorks
Tipo di EPrint:Tesi di dottorato
Relatore:Modesti, Michele
Dottorato (corsi e scuole):Ciclo 21 > Scuole per il 21simo ciclo > INGEGNERIA INDUSTRIALE > INGEGNERIA CHIMICA
Data di deposito della tesi:27 Gennaio 2009
Anno di Pubblicazione:Gennaio 2009
Parole chiave (italiano / inglese):polymer nanocomposites, carbon nanotubes, melt blending, processing conditions, organically modified layered silicates
Settori scientifico-disciplinari MIUR:Area 09 - Ingegneria industriale e dell'informazione > ING-IND/27 Chimica industriale e tecnologica
Struttura di riferimento:Dipartimenti > pre 2012 - Dipartimento di Processi chimici dell'Ingegneria
Codice ID:1460
Depositato il:27 Gen 2009
Simple Metadata
Full Metadata
EndNote Format

Bibliografia

I riferimenti della bibliografia possono essere cercati con Cerca la citazione di AIRE, copiando il titolo dell'articolo (o del libro) e la rivista (se presente) nei campi appositi di "Cerca la Citazione di AIRE".
Le url contenute in alcuni riferimenti sono raggiungibili cliccando sul link alla fine della citazione (Vai!) e tramite Google (Ricerca con Google). Il risultato dipende dalla formattazione della citazione.

[1] Qian D, Dickey EC, Andrews R, Rantell T. Appl Phys Lett. 76, 2000, 2868 Cerca con Google

[2] Andrews R, Jacques D, Minot M, Rantell T. Macrom Mater Eng. 287, 2002, 395 Cerca con Google

[3] Xia H, Wang Q, Hu GH. J Appl Polym Sci. 93, 2004 378 Cerca con Google

[4] Song YS, Youn JR. Carbon. 43, 2005, 1378 Cerca con Google

[5] Li C, Xiu-Jiang P, Zuo-Long Y. Mater Sci Eng A. 457, 2007, 287 Cerca con Google

[6] Satapathy BK, Weidisch R, Pötschke P, Janke A. Comp Sci Technol. 67, 2007, 867 Cerca con Google

[7] Reincke K, Grellmann W, Lach R, Heinrich G. Macromol Mater Eng. 288, 2003, 181 Cerca con Google

[8] Grellmann W, Reincke K, Lach R, Heinrich G. Kautschuk Gummi Kunststoffe. 54, 2001, 387 Cerca con Google

[9] Ajayan PM, Schadler LS, Braun PV. Nanocomposite Science andTechnology. Wiley-VCH Cerca con Google

GmbH & Co. (2004). Cerca con Google

[10] Meincke O, Kaempfer O, Weickmann H, Friedrich C, Vathauer M, Warth H. Polymer . 45, Cerca con Google

2004, 739 Cerca con Google

Studio di miscele polimeriche nanocomposite a matrice PC/ABS Cerca con Google

- 291 - Cerca con Google

[11] Modesti M, Besco S, Lorenzetti A, Causin V, Marega C, Gilman JW, Fox DM, Trulove PC, De Cerca con Google

Long HC, Zammarano M. Polym Degrad Stab. 92, 2007, 2206 Cerca con Google

[12] Eitan A, Fisher FT, Andrews R, Brinson LC, Schadler LS. Comp Sci Technol. 66, 2006, 1162 Cerca con Google

[13] Park SD, Han DH, Teng D, Kwon Y, Choi GW. J Korean Phys Soc. 48, 2006, 476 Cerca con Google

[14] McNally T, Pötschke P, Halley P, Murphy M, Martin D, Steven EJB, Brennan GP, Bein D, Cerca con Google

Lemoine P, Quinn JP. Polymer. 46, 2005, 8222 Cerca con Google

[15] Stretz HA, Paul DR, Cassidy PE. Polymer. 46, 2005, 3818 Cerca con Google

[16] Wang S, Hu Y, Song L, Wang Z, Chen Z, Fan W. Polym Degrad Stab. 77, 2002, 423 Cerca con Google

[17] Suzuki M, Wilkie CA. Polym Degrad Stab 47, 1995, 217. Cerca con Google

[18] Balart R, Sánchez L, Lòpez J, Jiménez A. Polym Degrad Stab. 91 2006 527 Cerca con Google

[19] Zeng Y, Ying Z, Du J, Cheng HM. J Phys Chem C. 111, 2007, 13945 Cerca con Google

[20] Kumar S, Rath T, Mahaling RN, Reddy CS, Das CK, Pandey KN, Srivastava RB, Yadaw SB. Cerca con Google

Mater Sci Eng B. 141, 2007, 61 Cerca con Google

[21] Siochi EJ, Dennis CW, Choel P, Peter TL, Jason HR, Crystal CT, Arup RB, Kumar S. Cerca con Google

Composite B. 35, 2004, 439. Cerca con Google

[22] Park C, Ounaies Z, Watson KA, Crooks R, Connell JW, Lowther SE, Siochi EJ, Harrison JS, Cerca con Google

Clair TL. Chem Phys Lett. 364, 2002, 303 Cerca con Google

[23] Li J, Tong L, Fang Z, Gu A, Xu Z. Polym Degrad Stab. 91, 2006, 2046 Cerca con Google

[24] Marosfi BB, Szabó A, Marosi G, Tabuani D, Camino G, Pagliari S, J Therm Anal Calor. 86, Cerca con Google

2006, 669 Cerca con Google

[25] Modesti M, Besco S, Lorenzetti A, Zammarano M, Causin V, Marega C, Gilman JW, Fox DM, Cerca con Google

Trulove PC, De Long HC, Maupin PH. Polymers for Advanced Technologies. 19, 2008, 1576 Cerca con Google

[25] Gilman JW. Appl Clay Sci. 15, 1999, 31 Cerca con Google

[26] Hu Y, Song L. International Fire Safety Conference (Fire Retardant Chemicals Association), Cerca con Google

11–14 March 2001. Cerca con Google

[27] Bourbigot S, Le Bras M, Dabrowski F, Gilman JW, Kashiwagi T. Fire Mater. 24, 2000, 201 Cerca con Google

[28] Owen SR, Harper JF. Polym Degrad Stab. 64, 1999, 449 Cerca con Google

[29] Jin Z, Wilkie CA. Polym Int. 49, 2000, 1158 Cerca con Google

[30] Gilman JW, Jackson CL, Morgan AB et al. Chem Mater. 12, 2000, 1866 Cerca con Google

[31] Pötschke P, Abdel-Goad M, Alig I, Dudkin SM, Lellinger D. Polymer. 45, 2004, 8863 Cerca con Google

[32] Pötschke P, Dudkin SM, Alig I. Polymer. 44, 2003, 5023 Cerca con Google

[33] Chen L, Pang XJ, Yu ZL. Mater Sci Eng A. 457, 2007, 287 Cerca con Google

[34] Paul et al. Polymer. 42, 2001, 9513. Cerca con Google

[35] Collins P, Hagerstrom J. Hyperion Catalysis International. Cerca con Google

[36] Basta M, Ricciarelli V, Stella R. Eur J Phys. 15, 1994, 97 Cerca con Google

[37] Stauffer D, Aharony A. Introduction to percolation theory. London, Taylor and Francis (1994). Cerca con Google

[38] Pötschke P, Abdel-Goad M, Alig I, Dudkin S, Lellinger D. J Non-Newtonian Fluid Mech. 128, Cerca con Google

2005, 2. Cerca con Google

CAPITOLO VIII Cerca con Google

- 292 - Cerca con Google

[39] Brandrup J, Immergut EH, Grulke EA. Polymer Handbook. John Wiley and Sons, New Cerca con Google

Jersey, 1999 Cerca con Google

[40] Pötschke P, Fornes TD, Paul DR. Polymer. 43, 2002, 3247 Cerca con Google

[41] Ray SS, Pouliot S, Bousmina M, Utracki LA. Polymer. 45, 2004, 8403 Cerca con Google

[42] Zhou O, Fleming RM, Murphy DW, Chen CH, Haddon RC, Ramirez AP. Science. 263, 1994, Cerca con Google

1744. Cerca con Google

[43] McClory, C., McNally, T., Brennan, G.P. and Erskine, J. Journal of Applied Polymer Science. Cerca con Google

46, 2006, 8222 Cerca con Google

[44] Dieckmann GR, Dalton AB, Johnson PA, Razal J, Chen J, Giordono GM, Munoz E, Cerca con Google

Musselman I, Baughman RH, Draper RJ. J. Am Chem Soc. 125, 2003, 1770. Cerca con Google

[45] Kodgire PV, Bhattacharyya AR, Bose S, Gupta N, Kulkarni AR, Misra A. Chem Phys Lett. Cerca con Google

432, 2006, 480 Cerca con Google

[46] Jin SH, Park YB, Yoon KH. Composites Science and Technology. 67, 2007, 3434 Cerca con Google

[47] Rao AM, Eklund PC, Bandow S, Thess A, Smalley RE. Nature. 388, 1997, 257 Cerca con Google

[48] Chen GX, Li Y, Shimizu H, Carbon. 45, 2007, 2327 Cerca con Google

[49] Reich S, Jantoljak H, Thomsen C. Phys Rev B. 61, 2000, 389 Cerca con Google

[50] Tuinstra F, Koenig JL. J Compos Mater. 4, 1970, 492 Cerca con Google

[51] Oberlin A. Chem Phys Carbon. 22, 1989, 1 Cerca con Google

[52] Tuinstra F, Koenig JL. J Chem Phys. 53, 1970, 1126 Cerca con Google

[53] Ferrari AC, Robertson J. Phys Rev B. 61, 2000, 14095 Cerca con Google

[54] Tomasella E, Thomas L, Meunier C, Nadal M, Mikhailov S. Surf Coat Technol. 360, 2003, Cerca con Google

174 Cerca con Google

[55] Tomasella E, Meunier C, Mikhailov S. Surf. Coat Technol. 141, 2001, 286 Cerca con Google

[56] Jayatissa AH, Sato F, Saito N, Ohnishi H, Takizawa K, Nakanishi Y, Yamaguchi T. Mater Cerca con Google

Sci Eng B. 55, 1998, 143 Cerca con Google

[57] Wu WY, Ting JM. Thin Solid Films. 166, 2002, 420 Cerca con Google

[58] Gilkes KWR, Sands HS, Batchelder DN, Robertson J, Milne WI. Appl Phys Lett 70, 1997, Cerca con Google

1980 Cerca con Google

[59] Yoshikawa M, Katagiri G, Ispida H, Ishitani A, Akamatsu T. Appl Phys Lett. 52, 1988, 1639 Cerca con Google

[60] Yoshikawa M, Katagiri G, Ishida H, Ishitani A, Akamatsu T. Solid State Comm. 66 ,1988, Cerca con Google

1177 Cerca con Google

[61] Scheibe J, Drescher D, Alers P. J Anal Chem. 353, 1995, 695. Cerca con Google

[62] Park M, Camphausen SM, Myers AF, Barletta PT, Sakhrani V, Bergman L, Nemanich RJ, Cerca con Google

Cuomo JJ. Mater Lett. 41, 1999, 229. Cerca con Google

[63] Fauteux C, Longtin R, Pegna J, Boman M. J Appl Phys. 95, 2004, 2737 Cerca con Google

[64] Mani RC, Sharma S, Sunkara MK, Gullapalli J, Baldwin RP, Rao R, Rao AM, Cowley JM. Cerca con Google

Electrochem Solid State Lett. 5, 2002, 32. Cerca con Google

[65] Tay BK, Shi X, Tan HS, Yang HS, Sun Z. Surf Coat Technol. 105, 1998, 155 Cerca con Google

Studio di miscele polimeriche nanocomposite a matrice PC/ABS Cerca con Google

- 293 - Cerca con Google

[66] Delhaes P, Couzi M, Trinquecoste M, Dentzer J, Hamidou H, Vix-Guterl C. Carbon 44, 2006, Cerca con Google

3005 Cerca con Google

[67] Smyth CP. Dielectric Behavior and Structure. McGraw-Hill, New York (1955). Cerca con Google

[68] Zhang YH, Dang ZM, Fu SY, Xin JH, Deng JG, Wu J, Yang S, Li LF, Yan Q. Chem Phys Lett. Cerca con Google

401, 2005, 553 Cerca con Google

[69] Liu C, Li C, Chen P, He J, Fan Q. Polymer. 45, 2004, 2803 Cerca con Google

[70] Steeman PAM, Turnhout JV. Macrom. 27, 1994, 5421 Cerca con Google

[71] Alegria A, Guerrica-Echevarria E, Goitiandia L, Telleria I, Colmenera J. Macrom. 28, 1995, Cerca con Google

1516 Cerca con Google

[72] Mertens IJA, Wubbenhorst M, Oosterbaan WD, Jenneskens LM, van Turnhout J. Macrom. Cerca con Google

32, 1999, 3314 Cerca con Google

[73] Bear E. Engineering design for plastics. New York (1974). Cerca con Google

[74] http://www.tainstruments.com Vai! Cerca con Google

[75] Fragneaud B, Masenelli Varlot K, González Montiel A, Terrones M, Cavaillé JY. Chem Phys Cerca con Google

Lett. 444, 2007, 1 Cerca con Google

[76] Barrau S, Demont P, Peignet A, Laurent C, Lacabanne C. Macrom. 36, 2003, 5187 Cerca con Google

[77] Dyre JC, Schroder TB. Rev Mod Phys. 72, 2000, 873 Cerca con Google

[78] Pourabas B, Raeesi V. Polymer. 46, 2005, 5533. Cerca con Google

[79] Wang S, Hu Y, Wang Z, Yong T, Chen Z, Fan W. Polym Degrad Stab. 80, 2003, 157 Cerca con Google

[80] Zong R, Hu Y, Wang S, Song L. Polym Degrad Stab. 83, 2004, 423 Cerca con Google

[81] Meincke O, Kaempfer D, Weickmann H, Friedrich C, Vathauer M, Warth H. Polymer. 45, Cerca con Google

2004, 739 Cerca con Google

[82] Zhang C, Han HF, Yi XS, Asai S, Sumita M. Compos Interf. 6, 1999, 227 Cerca con Google

[83] Zhang C, Han HF, Yi XS, Asai S, Sumita M. Mater Lett. 36, 1998, 186 Cerca con Google

[84] Soares BG, Gubbels F, Jerome R, Vanlathem E, Deltour R. Rubber Chem Technol. 70, 1997, Cerca con Google

60 Cerca con Google

[85] Park SJ, Jeong HJ, Nah C. Mat Sci Eng A. 385, 2004, 13 Cerca con Google

[86] Hu G, Meng X, Feng X, Ding Y, Zhang S, Yang M. J Mater Sci. 42, 2007, 7162. Cerca con Google

[87] Kaiser AB, Du¨sberg G, Roth S. Physical Review B. 57, 1998, 1418 Cerca con Google

[88] Treacy MMJ, Ebbesen TW, Gibson JM. Nature. 381, 1996, 678 Cerca con Google

[89] Wong EW, Sheehan PE, Lieber CM. Science. 277, 1997, 1971 Cerca con Google

[90] Berber S, Kwon Y-K, Tomanek D. Physical Review Letters. 84, 2000, 4613 Cerca con Google

[91] Donnet J, Bansal R, Wang M. Carbon black: science and technology. New York: Marcel Cerca con Google

Dekker, 1993. Cerca con Google

[92] Garboczi EJ, Snyder KA, Douglas JF, Thorpe MF. Physical Review E. 52, 1995, 819 Cerca con Google

[93] Potschke P, Bhattacharyya AR, Janke A, Pegel S, Leonhardt A, Taschner C, et al. Fullerenes, Cerca con Google

Nanotubes and Carbon Nanostructures. 13, 2005, 211 Cerca con Google

[94] Lin B, Sundararaj U, Potschke P. Macromolecular Materials and Engineering. 291, 2006, 227 Cerca con Google

[95] Potschke P, Bhattacharyya AR, Janke A. European Polymer Journal. 40, 2004, 137 Cerca con Google

CAPITOLO VIII Cerca con Google

- 294 - Cerca con Google

[96] Dondero WE, Gorga RE. Journal of Polymer Science, Part B: Polymer Physics 44, 2006, 864 Cerca con Google

[97] Li Y, Shimizua H. Polymer. 48, 2007, 2203 Cerca con Google

[98] Andrews R, Jacques D, Minot M, Rantell T. Macromolecular Materials Cerca con Google

and Engineering. 287, 2002, 395 Cerca con Google

[99] Ferguson DW, Bryant EWS, Fowler HC. ESD thermoplastic product offers advantages for Cerca con Google

demanding electronic applications. Atlanta: ANTEC, 1998, 1219 Cerca con Google

[100] Potschke P, Brunig H, Janke A, Fischer D, Jehnichen D. Polymer, 46, 2005, 10355 Cerca con Google

[101] Potschke P, Bhattacharyya AR, Janke A, Goering H. Composite Interfaces. 10, 2003, 389 Cerca con Google

[102] Potschke P, Dudkin SM, Alig I. Polymer. 44, 2003, 5023 Cerca con Google

[103] S. Pegel et al. Polymer. 9, 2008, 97 Cerca con Google

[104] Filippone G, Dintcheva N, Acierno D, La Mantia FP. Polymer. 49, 2008, 1312 Cerca con Google

[105] Al-Saleh MH, Sundararaj U. Composites: Part A 39, 2008, 284 Cerca con Google

[106] S. Peeterbroeck et al. Composites Science and Technology 64, 2004, 2317 Cerca con Google

[107] Fornes TD, Paul DR, Polymer 44 (2003) 4993 Cerca con Google

[108] http://www.sunnano.com Vai! Cerca con Google

[109] http://webmineral.com Vai! Cerca con Google

[110] Prashantha K et al., Compos Sci Technol (2008), doi:10.1016/j.compscitech.2008.10.005) – in Cerca con Google

press Cerca con Google

[111] Satapathy BK, Weidisch R, Pötschke P, Janke A. Comp. Sci and Tech. 67, 2007, 867 Cerca con Google

[112] Ajayan PM, Schadler L, Pbraun PV, Nanocomposite science and technology, Wiley-VCH Cerca con Google

Verlag (2003) Cerca con Google

[113] Cooper CA, Cohen SR, Barber AH, Wagner HD. Appl Phys Lett. 81, 2002, 3873 Cerca con Google

[114] Pötschke P, Bhattacharya AR, Janke A. Polymer. 44 2003, 8061 Cerca con Google

[115] Xia Z, Riester L, Curtin WA, Li H, Sheldon BW, Liang J et al. Acta Mater. 52, 2004, 931 Cerca con Google

[116] Vaia RA, Giannellis EP. Macromolecules. 30, 1997, 7990 Cerca con Google

[117] Koo CM, Ham SO, Kim KH, Wang IJ, Chung D, Kim D, Zin W. Macromolecules. 35, 2002, Cerca con Google

5116 Cerca con Google

[118] Maiti P, Nam PH, Okamoto M, Hasegawa N, Usuki A. Macromolecules. 35, 2002, 2042 Cerca con Google

[119] Klug HP, Alexander LE. X-Ray diffraction procedure. 1974, John Wiley & Sons, New York Cerca con Google

[120] Causin V, Marega C, Marigo A, Ferrara G. Polymer. 46, 2005, 9533 Cerca con Google

[121] Brindley GW, Brown G. Crystal structure of clay minerals and their X-Ray identification. Cerca con Google

1980, Mineralogical Society, London Cerca con Google

[122] Yoon PJ, Fornes TD, Paul DR. Polymer 43, 2002, 6727 Cerca con Google

[123] Guth E, Gold 0. Phys. Rev. 53, 1938, 322 Cerca con Google

[124] Guth E. J. Appl. Phys. 16, 1945, 20 Cerca con Google

[125] Halpin JC. J Compos Mater. 3, 1969, 732 Cerca con Google

[126] Halpin JC, Kardos JL. Polym Eng Sci. 16, 1976, 344 Cerca con Google

[127] Hermans J. Proc Kon Ned Akad v Wetensch B. 65, 1967, 1 Cerca con Google

[128] Hill R. J Mech Phys Solids. 12, 1964, 119 Cerca con Google

Studio di miscele polimeriche nanocomposite a matrice PC/ABS Cerca con Google

- 295 - Cerca con Google

[129] Mori T, Tanaka K. Acta Metall. 21, 1973, 571 Cerca con Google

[130] Eshelby JD. Proc Roy Soc Long. 2, 1957, 376 Cerca con Google

[131] Tandon GP, Weng GJ. Polym Compos. 5, 1984, 327 Cerca con Google

[132] Vlasveld DPN, Fibre reinforced polymer nanocomposites, Ph.D dissertation, 2005 Cerca con Google

[133] Foye R. SAMPE. 10, 1966, 31 Cerca con Google

[134] Ashton JE, Halpin JC, Petit PH. Primer on composite materials: analysis. Stamford, Conn: Cerca con Google

Techomic Pub. Co; 1969 Cerca con Google

[135] Adams D, Doner D. J Compos Mater. 1, 1967, 152 Cerca con Google

[136] Alexandre M, Dubois P. Mater. Sci. Eng. 28, 2000, 1 Cerca con Google

[137] Wu et al., Polymer Testing. 23, 2004, 903 Cerca con Google

[138] Chavarria F, Paul DR. Polymer. 45, 2004, 8501 Cerca con Google

[139] Paul DR, Roberson LM. Polymer. 49, 2008, 3187 Cerca con Google

[140] Garofalo E. Effect of extensional flow on morphology and properties of polyamide layered Cerca con Google

silicate nanocomposites. Ph.D. dissertation, 2008 Cerca con Google

[141] Luo JJ, Daniel IM. Composites Science and Technology. 63, 2003, 1607 Cerca con Google

[142] Brune DA, Bicerano J. Polymer. 43, 2002, 369 Cerca con Google

Solo per lo Staff dell Archivio: Modifica questo record