Piga, Matteo (2012) New hybrid inorganic-organic proton conducting membranes for PEMFC: synthesis, properties and conduction mechanisms. [Ph.D. thesis]

Full text disponibile come:

[img]
Preview
PDF Document - Draft Version
20Mb

Abstract (english)

Electrochemical devices for the conversion of chemical energy into electrical power, such as proton exchange membrane fuel cells (PEMFCs), are of intense interest to industry and the scientific community because of their high energy conversion efficiency, low environmental impact, and the possibility for use in a wide variety of applications from portable electronic devices to light-duty electric vehicles. At the core of the fuel cell is a PEM that allows the transport of hydrogen ions, evolved at the anode, to the cathode where oxygen is reduced to water. Todays prevalent PEMs feature perfluorinated main chains functionalized with perfluoroether side chains terminated with acidic -SO3H groups. These materials (DupontTM Nafion®, Asashi Aciplex®, Dow®, and Flemion®) generally are characterized by a high chemical, thermal and mechanical stability; they also exhibit good proton conductivity at high levels of hydration. The hydration requirements limit the widespread commercial use of conventional PEMs, which have inadequate proton conductivity at temperatures above 90C and at low values of relative humidity. Fuel cells capable of operating above 120C at low levels of hydration would: obviate the need of bulky and expensive water management modules, simplify thermal management; and reduce the impact of catalyst poisons such as carbon monoxide. In an effort to overcome the limitations of conventional PEMs, this work reports the synthesis and characterization of new proton conducting membrane alternatives to classic fluorinated polymers for application in PEMFCs. The materials were synthesized according to two distinct strategies: 1) dope a Nafion membrane in order to improve its thermo-mechanical properties and proton conductivity or extend its operating conditions to temperatures above 100°C and an anhydrous environment; 2) synthesize and characterize proton exchange membranes based on polybenzimidazole and polysulfone as an alternative to perfluorinated polymers.
The first point regarded the study of two different systems obtained by doping a Nafion membrane with the [(ZrO2)(Ta2O5)0.119] inorganic “core-shell” nanofiller or with two different proton conducting ionic liquids, triethylammonium methanesulfonate and triethylammonium perfluorobutanesulfonate. The study of new PEMs alternative to fluorinated polymers has been developed considering polybenzimidazole and sulfonated poly(p-phenylenesulfone) membranes whose properties have been modulated by the addition of phosphoric acid and an hybrid filler or poly(1-oxotrimethylene) and silica, respectively. All the proposed materials were extensively characterized in terms of their thermal, mechanical, structural and electrical properties in order to highlight the interactions between the different components present within the membranes. These interactions govern the membranes macroscopic properties that need to be improved in order to optimize and predict the behavior of these materials under operating conditions in fuel cells.

Abstract (italian)

Celle a combustibile basate su membrane a scambio protonico (PEMFCs) sono dispositivi elettrochimici per la conversione di energia chimica in energia elettrica. Le PEMFCs suscitano notevole interesse sia nel mondo industriale che accademico a causa della loro elevata efficienza di conversione, basso impatto ambientale e vasta gamma di utilizzo che spazia dall’elettronica portatile fino all’autotrazione.
All’interno della cella a combustibile si trova la membrana a scambio protonico (PEM), che consente il trasferimento di protoni dall’anodo al catodo.
Attualmente le membrane polimeriche a scambio protonico maggiormente utilizzate sono costituite da polimeri fluorurati funzionalizzati con gruppi polieterei terminanti con gruppi acidi (tipicamente -SO3H). Questi materiali (DupontTM Nafion®, Asashi Aciplex®, Dow®, and Flemion®) generalmente presentano elevata stabilità chimica, termica e meccanica ma tuttavia mostrano valori di conducibilità sufficienti per il loro impiego in cella a combustibile solo per elevati livelli di idratazione. La scarsa conducibilità protonica dei polimeri perfluorurati per temperature maggiori di 90°C e bassi livelli di idratazione limita fortemente il loro utilizzo su larga scala.
Celle a combustibile che operano a temperature superiori a 120°C e bassi livelli di idratazione non necessitano dell’introduzione di sistemi di umidificazione e raffreddamento, riducendo il costo e semplificando la realizzazione ed ingegnerizzazione del dispositivo finale. Inoltre, l’aumento di temperatura riduce l’avvelenamento del catalizzatore da contaminanti esterni come ad esempio il monossido di carbonio.
Al fine di superare le limitazioni delle PEMs convenzionali, questo lavoro di tesi riporta la sintesi e la caratterizzazione di nuove membrane polimeriche a conducibilità protonica alternative ai classici polimeri fluorurati per applicazioni in celle a combustibile.
I materiali sono stati sintetizzati seguendo due diverse strategie: 1) drogare una membrane di Nafion al fine di aumentare il suo intervallo di stabilità termico e meccanico e la sua conducibilità protonica così da estenderne le condizioni operative di utilizzo a temperature maggiori di 90°C e per bassi o nulli livelli di idratazione; 2) sintetizzare e caratterizzare PEMs basate su polibenzimidazolo e polisulfone come materiali alternativi ai classici polimeri fluorurati.
Il primo punto ha riguardato lo studio di due diversi sistemi ottenuti drogando una membrana di Nafion con il filler inorganico [(ZrO2)(Ta2O5)0.119] oppure con due diversi liquidi ionici a conducibilità protonica, il trietilammonio-metansolfonato ed il trietilammonio-perfluorobutansolfonato.
Lo studio di nuove membrane alternative ai polimeri fluorurati è stato sviluppato considerando membrane di polibenzimidazolo (PBI) e polisulfone solfonato (sPSO2) le cui proprietà sono state modulate dall’aggiunta di acido fosforico e di un filler ibrido a base di silice funzionalizzata (nel caso del PBI) o di poliossotrimetilene e silice (per le membrane a base di sPSO2).
Al fine di delucidare le interazioni esistenti tra i diversi componenti presenti all’interno delle membrane, tutti i materiali sono stati ampiamente caratterizzati dal punto di vista delle loro proprietà termiche, meccaniche, strutturali ed elettriche. Queste interazioni governano le proprietà macroscopiche delle membrane che necessitano di essere migliorate al fine di ottimizzare e prevedere il comportamento di questi materiali in condizioni di esercizio in celle a combustibile.

Statistiche Download
EPrint type:Ph.D. thesis
Tutor:Di Noto, Vito
Ph.D. course:Ciclo 24 > Scuole 24 > SCIENZA ED INGEGNERIA DEI MATERIALI
Data di deposito della tesi:11 January 2012
Anno di Pubblicazione:11 January 2012
Key Words:Fuel Cell, Proton Exchange Membrane, Nafion, Ionic Liquid, polybenzimidazole, sulfonated polysulfone, Broadband Electric Spectroscopy, proton conduction mechanisms
Settori scientifico-disciplinari MIUR:Area 03 - Scienze chimiche > CHIM/05 Scienza e tecnologia dei materiali polimerici
Struttura di riferimento:Dipartimenti > Dipartimento di Scienze Chimiche
Codice ID:4356
Depositato il:20 Dec 2012 14:04
Simple Metadata
Full Metadata
EndNote Format

Bibliografia

I riferimenti della bibliografia possono essere cercati con Cerca la citazione di AIRE, copiando il titolo dell'articolo (o del libro) e la rivista (se presente) nei campi appositi di "Cerca la Citazione di AIRE".
Le url contenute in alcuni riferimenti sono raggiungibili cliccando sul link alla fine della citazione (Vai!) e tramite Google (Ricerca con Google). Il risultato dipende dalla formattazione della citazione.

1. US Energy Information Administration, Petroleum and Other Liquids, http://www.eia.gov/dnav/pet/hist/LeafHandler.ashx?n=PET&s=WTOTWORLD&f=W, accessed on August 28, 2011. Vai! Cerca con Google

2. Vielstich W.; Ideal and effective efficiencies of cell reactions and comparison to Carnot cycles. In: W. Vielstich; AL, H. A. Gasteiger; editor, Handbook of Fuel Cells – Fundamentals, technology and applications. Vol 1. Chichester: John Wiley & Sons; 2003, p. 26. Cerca con Google

3. Satyapal S.; Hydrogen and Fuel Cell Activities. 5th International Conference on Polymer Batteries & Fuel Cells, Argonne, Illinois: US Department of Energy: Energy Efficiency & Renewable Energy; 2011. Cerca con Google

4. Nguyen, T.; Ward, J.; Well-to-Wheels Greenhouse Gas Emissions and Petroleum Use for Mid-Size Light-Duty Vehicles: US Department of Energy: Offices of Vehicle Technologies & Fuel Cell Technologies, 2010. Cerca con Google

5. Hamnett, A.; Introduction to fuel-cell types, In: W. Vielstich, AL, H. A. Gasteiger, editor, Handbook of Fuel Cells – Fundamentals, technology and applications. Vol 1. Chichester: John Wiley & Sons; 2003, p. 36. Cerca con Google

6. Sandstede, G.; Cairns, E.J.; Bagotsky, V.S.; Wiesener, K.; History of low-temperature fuel cells, In: W. Vielstich, AL, H. A. Gasteiger editor, Handbook of Fuel Cells – Fundamentals, technology and applications. Vol 1. John Wiley & Sons, Chichester; 2003, p. 145. Cerca con Google

7. Smitha, B.; Sridhar, S.; Khan, A.A.; J. Membr. Sci. 2005; 259, 10. Cerca con Google

8. Laberty-Robert, C.; Valle, K.; Pereira, F.; Sanchez, C.; Chem. Soc. Rev. 2011; 40, 961. Cerca con Google

9. Epping, M.K.; Kopasz, J.P.; The U.S. DOEs High Temperature Membrane Effort. Fuel Cells 2009; 9, 356. Cerca con Google

10. Boeing Successfully Flies Fuel Cell-Powered Airplane, Boeing, http://www.boeing.com/news/releases/2008/q2/080403a_nr.html, accessed on August 28, 2011. Vai! Cerca con Google

11. Clean Energy Patent Growth Index, Cleantech Group, Heslin Rothenberg Farley & Mesiti P.C., http://cepgi.typepad.com/heslin_rothenberg_farley_/, accessed on August 28, 2011. Vai! Cerca con Google

12. Doyle, M.; Rajendran, G.; Perfluorinated membranes, In: W. Vielstich, AL, H. A. Gasteiger, editor, Handbook of Fuel Cells – Fundamentals, technology and applications. Vol 3. Chichester: John Wiley & Sons; 2003, p. 351. Cerca con Google

13. Grot, W.; Fluorinated ionomers. Norwich, NY: William Andrew 2008. Cerca con Google

14. Mauritz, K. A.; Moore R. B.; Chem. Rev. 2004; 104, 4535. Cerca con Google

15. Rubatat, L.; Rollet, A. L.; Gebel, G.; Diat, O., Macromolecules 2002, 3, 4050. Cerca con Google

16. Chen, Q.; Schmidt-Rohr, S.; Macromol. Chem. Phys., 2007, 208, 2189. Cerca con Google

17. Iojoiu, C.; Chabert, F.; Marechal, M.; Kissi, N.E.; Guindet, J.; Sanchez, J-Y; J. Power Sources 2006, 153, 198. Cerca con Google

18. Sanchez, J-Y; Alloin, F.; Iojoiu, C.; J. Fluorine Chem. 2006, 127, 1471. Cerca con Google

19. Asensio, J.A.; Sanchez, E.M.; Gomez-Romero, P.; Chem. Soc. Rev. 2010, 39, 3210. Cerca con Google

20. Li, Q.; He, R.; Jensen ,J.O.; Bjerrum, N.J.; Chem. Mater. 2003, 15, 4896. Cerca con Google

21. Bose, S.; Kuila, T.; Nguyen T.X.H.; Kim, N.H.; Lau K-t; Lee, J.H.; Prog. Polym. Sci. 2011, 36, 813. Cerca con Google

22. Ahmad, H.; Kamarudin, S.K.; Hasran, U.A.; Daud, W.R.W.; Int. J. Hydrogen Energy 2010, 35, 2160. Cerca con Google

23. Hickner, M.A.; Ghassemi, H.; Kim, Y.S.; Einsla, B.R.; McGrath, J.E; Chem. Rev. 2004, 104, 4587. Cerca con Google

24. Hamrock, S.; Membranes and MEAs for Dry, Hot Operating Conditions: 2010 Annual Progress Report: DOE Hydrogen Program; 2011. Cerca con Google

25. Souzy, R.; Ameduri, B.; Boutevin, B.; Gebel, G.; Capron, P.; Solid State Ionics 2005; 176, 2839. Cerca con Google

26. Lee, J.S.; Quan, N.D.; Hwang, J.M.; Lee, S.D.; Kim, H.; Lee, H. et al., J. Ind. Eng. Chem. 2006; 12, 175. Cerca con Google

27. Rikukawa, M.; Sanui, K.; Prog. Polym. Sci. 2000; 25, 1463. Cerca con Google

28. Akbarian-Feizi, L.; Mehdipour-Ataei, S.; Yeganeh, H.; Int. J. Hydrogen Energy 2010; 35, 9385. Cerca con Google

29. Gubler, L.; Kramer, D.; Belack, J.; Unsal, O.; Schmidt, T.,J.; Scherer, G.G.; Celtec, V.; J. Electrochem. Soc. 2007; 154, B981. Cerca con Google

30. Herring, A.M.; Polymer Reviews 2006; 46, 245. Cerca con Google

31. Alberti, G.; Casciola, M.; Annu. Rev. Mater. Res. 2003; 33, 129. Cerca con Google

32. Di Noto, V.; Gliubizzi, R.; Negro, E; Vittadello, M.; Pace, G; Electrochim Acta 2007; 53, 1618. Cerca con Google

33. Di Noto, V.; Lavina, S.; Negro, E.; Vittadello, M.; Conti, F.; Piga, M. et al., J Power Sources 2009; 187, 57. Cerca con Google

34. Sahu, A.K.; Pitchumani, S.; Sridhar, P.; Shukla, A.K.; Bull. Mater. Sci. 2009; 32, 285. Cerca con Google

35. Di Noto, V.; Piga, M.; Lavina, S.; Negro, E.; Yoshida, K.; Ito, R.; Furukawa, T.; Electrochim. Acta 2010; 55, 1431. Cerca con Google

36. Di Noto, V.; Piga, M.; Piga, L.; Polizzi, S.; Negro, E.; J. Power Sources, 2008, 178, 561. Cerca con Google

37. Di Noto, V.; Boaretto, N.; Negro, E.; Giffin G.A.; Lavina, S.; Polizzi, S.; Int. J. Hydrogen Energy 2011;doi:10.1016/j.ijhydene.2011.07.132. Cerca con Google

38. Di Noto, V.; Boaretto, N.; Negro, E.; Stallworth, P.E.; Lavina, S.; Giffin, G.A.; Greenbaum, S. G.; Int. J. Hydrogen Energy 2011; doi:10.1016/j.ijhydene.2011.07.135. Cerca con Google

39. Fernandez-Carretero, F.J.; Compan, V.; Riande, E.; J. Power Sources 2007; 173, 68. Cerca con Google

40. Navarra, M.A.; Croce, F.; Scrosati, B.; J. Mater. Chem. 2007; 17, 3210. Cerca con Google

41. Meng, F.; Aieta, N.V.; Dec, S.F.; Horan, J.L.; Williamson, D.; Frey, M.H. et al. Electrochim. Acta 2007; 53, 1373. Cerca con Google

42. Horan, J.L.; Genupur, A.; Ren, H.; Sikora, B.J.; Kuo, M.C.; Meng, F. et al., ChemSusChem 2009; 2, 226. Cerca con Google

43. Herring, A.M.; Horan, J.L.; Kuo, M-C.; Ziegler, Z.C.; Zhang F, Perdue, A.S. et al., Novel Approaches to Immobilized Heteropoly Acid (HPA) Systems for High Temperature, Low Relative Humidity Polymer-Type Membranes: 2010 Annual Progress Report: DOE Hydrogen Program; 2011. Cerca con Google

44. Greaves, T.L.; Drummond, C.J.; Chem. Rev. 2008; 108, 206. Cerca con Google

45. Angell, C.A.; Xu, W.; Yoshizawa, M.; Hayashi, A.; Belieres, J-P.; Lucas, P. et al., Physical Chemistry of Ionic Liquids, Inorganic, Organic, Protic and Aprotic, In: Ohno, H, editor, Electrochemical Aspects of Ionic Liquids. 1st ed. Vol Hoboken, NJ: Wiley-Interscience; 2005, p. 5-23. Cerca con Google

46. Thiam, H.S.; Daud, W.R.W.; Kamarudin, S.K.; Mohammad, A.B.; Kadhum, A.A.H.; Loh, K.S. et al., Int. J. Hydrogen Energy 2011; 36, 3187. Cerca con Google

47. Allcock, H.R.; Solid State Mater. Sci. 2007; 10, 231. Cerca con Google

48. Allcock, H.R.; Wood, R.M.; J. Polym. Sci., Part B: Polym. Phys. 2006; 44, 2358. Cerca con Google

49. Premchand, Y. D.; Di Vona, M. L.; Knauth, P.; Proton-Conducting Nanocomposites and Hybrid Polymers, in: Knauth, P.; Schoonman, J.; editors, Nanocomposites: ionic conducting materials and structural spectroscopies, Springer, 2007, p. 77. Cerca con Google

50. Peckham, T.J.; Yang, Y.; Holdcroft, S.; Proton Exchange Membranes in: Wilkinson, D. P.; Zhang, J.; Hui, R.; Fergus, J.; Li, X.; editors, Proton Exchange Membrane Fuel Cells: Materials Properties and Performance, CRC Press Taylor&Francis Group, 2010, p. 107. Cerca con Google

51. Ratner, M.; in Polymer Electrolytes Reviews; MacCallum, J. R.; Vincent, C. A., eds.; Elsevier: London, 1987. Cerca con Google

52. Ediger, M. D.; Angell, C. A.; Nagel, S. R.; J. Phys. Chem., 1996 , 100, 13200. Cerca con Google

53. Ratner, M. A.; Shriver, D. F.; Chemical Reviews, 1988, 88, 109. Cerca con Google

54. Di Noto, V.; Negro, E.; Sanchez, J. Y.; Iojoiu, C., J. Am. Chem. Soc. 2010, 132, 2183. Cerca con Google

55. Giffin, G. A.; Piga, M.; Lavina, S.; Navarra, M. A.; D’Epifanio, A.; Scrosati, B.; Di Noto, V.; J. Power Sources, 2012, 198, 66. Cerca con Google

56. Di Noto, V.; Piga, M.; Giffin, G. A.; Pace, G.; J. Membr. Sci., 2012, 390, 58. Cerca con Google

Download statistics

Solo per lo Staff dell Archivio: Modifica questo record