Ferraro, Stefano (2014) Influence of trace elements on secondary die-cast aluminium alloys. [Tesi di dottorato]

Full text disponibile come:

[img]
Anteprima
Documento PDF
4Mb

Abstract (inglese)

Recycling play a key role on saving of natural resources and on reducing pollution. The recycling of aluminium alloys is also cost-effective, since it reduce the material cost and creates a considerable energy-saving. The use of recycled Al alloys (usually called secondary) has improved in recent years also because of their comparable mechanical properties with primary aluminium alloys.
During the production of secondary aluminium alloys, the scrap are mixed regardless of their specific chemical composition, and then master alloys or pure elements are added to the molten metal. Furthermore, certain impurity elements are either difficult or expensive to remove, and their role in mechanical properties can be important. Due to the presence of these additional trace elements, a number of complex intermetallic phases can therefore form in multi-component Al-Si alloys. Mechanical and physical properties of alloys and castings are strongly related to sizes, morphologies and distribution of these intermetallic phases, which are in turn a function of alloy composition and cooling rate.
The Al–Si based alloys are transversally used in different foundry processes. Among all the technologies, high-pressure die-casting (HPDC) represents the most common process to produce automotive components by secondary Al–Si alloys because it allows one to increase the production by lowering the cycle time and to obtain economically components with complex geometries and high quality surface.
The effects of trace elements and intermetallics phases on features of aluminium castings are still not fully understood, especially when components are made by means of HPDC process. The motivation of the research presented in this doctoral thesis was, therefore, to fill this gap in knowledge. The study has aimed at understanding the influence of various trace elements on the microstructure and mechanical properties of secondary die-cast aluminium alloys and, in particular, on secondary AlSi9Cu3(Fe) die-cast alloys.
A literature review and a sufficient background of previously reported results on the influence of trace elements on the features of aluminium alloys as well as the formation of intermetallic phases were carried out. It was found that the mechanical and microstructural analysis generally referred to primary cast Al alloys with low concentration of trace elements outside of those studied. Furthermore the samples were usually produced on gravity die-cast, while some intermetallics phases were frequently observed in high-pressure die-casting, where higher cooling rates and different feeding conditions exist.
Special attention has been given to:
The effects of Bismuth addition on secondary die-cast aluminium alloys: Bismuth substitute the lead in free-cutting wrought Al alloys, and this is leading to a steady increase of Bi content in secondary Al alloys due to the recycling process.
The nucleation temperature of primary Fe-rich intermetallic compounds, as function of Fe, Mn and Cr content and cooling rate: Fe-rich phases have a high specific gravity and tend to segregate to the bottom of aluminium melts and holding furnaces. These phases form primary solid particles, generally called sludge, thus reduce the effective capacity of the furnace.
The influence of Fe, Mn and Cr addition, separately or in combination, on the microstructural and mechanical characteristics of secondary die-cast aluminium alloys: sludge crystals are hard and brittle compact inclusions which can compromise the machining operations, with a considerable effects on the cutting tool life, and even more degrade the mechanical and physical properties of the component. As recycling of aluminium alloys becomes more common, sludge will be a problem of increasing importance due to the concentration of Fe, Mn and Cr in the scrap cycle.

Abstract (italiano)

Il riciclaggio gioca un ruolo chiave sul risparmio delle risorse naturali e sulla riduzione dell'inquinamento. Il riciclo dell'alluminio è oltretutto economicamente conveniente, in quanto riduce il costo del materiale a fronte di un considerevole risparmio energetico. L'utilizzo di leghe di alluminio riciclate (comunemente chiamate leghe secondarie) è aumentato negli ultimi anni anche grazie alle loro proprietà meccaniche, le quali sono in alcuni casi comparabili con le leghe di alluminio primarie.
Durante il processo di produzione dell'alluminio secondario i rottami vengono mescolati assieme indipendentemente dalla loro composizione chimica specifica. Al termine del processo fusorio la composizione viene regolata tramite l'aggiunta di leghe madri o di metalli puri. Tuttavia alcune impurezze presenti nel rottame rimangono all'interno della lega in quanto il loro processo di rimozione è complicato o non economicamente conveniente. A causa della presenza di questi elementi in traccia, un certo numero di fasi intermetalliche complesse si può formare nei getti. Di conseguenza le proprietà meccaniche e fisiche dei componenti in lega di alluminio sono fortemente correlate alla dimensione, alla morfologia e alla distribuzione di tali fasi intermetalliche, le quali sono a loro volta funzione della composizione della lega e della velocità di raffreddamento del metallo.
Grazie alle loro elevata colabilità, le leghe Al-Si sono molto utilizzate in tutti i processi di fonderia. Tra le diverse tecnologie, la pressocolata (HPDC - high-pressure die-casting) rappresenta il processo più comune per la produzione di getti di alluminio nel settore automotive. Questa tecnologia permette di ottenere componenti con geometrie complesse e un'ottima finitura superficiale con una riduzione dei costi grazie alla elevata produttività e al basso tempo ciclo.
Gli effetti degli elementi in traccia e delle fasi intermetalliche sulle proprietà dei getti in alluminio non sono ancora del tutto noti, soprattutto quando i componenti sono prodotti tramite pressocolata. Obiettivo di questo lavoro di dottorato di ricerca era perciò quello di supplire a queste lacune. Lo scopo del presente lavoro è studiare l'influenza di diversi elementi in traccia sulla microstruttura e sulle proprietà meccaniche di getti in lega secondaria di alluminio prodotti mediante pressocolata, ed in particolare nella lega AlSi9Cu3(Fe).
In prima analisi, è stata condotta una recensione della letteratura sull'influenza degli elementi in traccia sulle proprietà delle leghe di alluminio e sulla formazione delle fasi intermetalliche. Questo ha permesso di constatare che le caratteristiche meccaniche e microstrutturali legate alla presenza di fasi indesiderate sono normalmente valutate in getti prodotti con leghe primarie di alluminio, in cui è presente una bassa concentrazione di impurezze al di fuori di quelle studiate. Inoltre i campioni studiati sono generalmente prodotti mediante colata in gravità, mentre alcune fasi intermetalliche sono tipiche della pressocolata, in cui la velocità di raffreddamento è molto più elevata e sono presenti diverse condizioni di alimentazione e di riempimento dello stampo.
Nel presente lavoro è stata posta particolare attenzione a:
Gli effetti dell'aggiunta di Bismuto nelle leghe di alluminio secondarie pressocolate: il Bismuto ha sostituito il Piombo nelle leghe di alluminio da deformazione plastica ad alta lavorabilità alle macchine utensile. Questo ha comportato un aumento del contenuto di Bismuto nelle leghe secondarie di alluminio a causa del processo di riciclaggio degli sfridi di lavorazione.
La temperatura di nucleazione dei precipitati intermetallici ricchi in Ferro in funzione della velocità di raffreddamento e della concentrazione in lega di Ferro, Cromo e Manganese: le fasi ricche in ferro hanno un elevata densità e tendono a segregare sul fondo del fondo del forno di mantenimento. L'insieme di queste fasi primarie forma una fanghiglia, chiamata sludge, che riduce l'effettiva capacità del forno.
L'effetto dell'aggiunta di Ferro, Cromo e Manganese, singolarmente o in combinazione tra di loro, sulle caratteristiche microstrutturali e meccaniche delle leghe di alluminio secondarie pressocolate: le particelle di sludge sono inclusioni compatte dure e fragili, le quali possono compromettere le operazioni di lavorazione meccanica, con una conseguente riduzione della durata degli utensili, ed una marcata riduzione delle proprietà meccaniche e fisiche del componente. Il problema delle particelle di sludge nelle leghe secondarie di alluminio assume un'importanza sempre maggiore a causa dell'aumento del riciclo dell'alluminio e della presenza di Fe, Mn e Cr nel ciclo del rottame.

Statistiche Download - Aggiungi a RefWorks
Tipo di EPrint:Tesi di dottorato
Relatore:Timelli, Giulio
Dottorato (corsi e scuole):Ciclo 26 > Scuole 26 > INGEGNERIA MECCATRONICA E DELL'INNOVAZIONE DEL PRODOTTO
Data di deposito della tesi:28 Gennaio 2014
Anno di Pubblicazione:28 Gennaio 2014
Parole chiave (italiano / inglese):Aluminium alloys, Recycling, Microstructure, Mechanical properties, High-pressure die-casting, Sludge Factor, Fe-rich intermetallics, Iron, Manganese, Chromium, Bismuth, trace elements, DSC, Thermal Analysis, Cooling Rate, DOE, ANOVA
Settori scientifico-disciplinari MIUR:Area 09 - Ingegneria industriale e dell'informazione > ING-IND/21 Metallurgia
Struttura di riferimento:Dipartimenti > Dipartimento di Tecnica e Gestione dei Sistemi Industriali
Codice ID:6522
Depositato il:13 Nov 2014 09:53
Simple Metadata
Full Metadata
EndNote Format

Bibliografia

I riferimenti della bibliografia possono essere cercati con Cerca la citazione di AIRE, copiando il titolo dell'articolo (o del libro) e la rivista (se presente) nei campi appositi di "Cerca la Citazione di AIRE".
Le url contenute in alcuni riferimenti sono raggiungibili cliccando sul link alla fine della citazione (Vai!) e tramite Google (Ricerca con Google). Il risultato dipende dalla formattazione della citazione.

[1] M.E. Schlesinger: 'Aluminum Recycling', USA, Taylor & Francis, (2007). Cerca con Google

[2] S.K. Das: 'Designing Aluminum Alloys for a Recycling Friendly World', Mater. Sci. Forum, vol.519-521, pp.1239-1244, (2006). Cerca con Google

[3] J.G. Kaufman and E.L. Rooy: 'Aluminum Alloy Castings: Properties, Processes, and Applications', pp.340; USA, ASM International, (2004). Cerca con Google

[4] J. Zehnder, R. Pritzlaff, S. Lundberg, and B. Gilmont: 'Aluminium in Commercial Vehicles', 9th ed., European Aluminium Association, (1988). Cerca con Google

[5] EAA: 'Aluminium in Cars', 1st ed., pp.1-15; European Aluminium Association, (2007). Cerca con Google

[6] J.E. Gruzleski and B.M. Closset: 'The treatment of liquid aluminum-silicon alloys', USA, American Foundrymen's Society, Inc., (1990). Cerca con Google

[7] J.L. Murray and A.J. McAlister: 'The Al-Si (Aluminum-Silicon) system', Bulletin of Alloy Phase Diagrams, vol.5(1), pp.74-84, (1984). Cerca con Google

[8] L. Backerud, G. Chai, and J. Tamminen: 'Solidification Characteristics of Aluminum Alloys, vol 2: Foundry Alloys', pp.266; Stockholm, AFS-Skanaluminium, (1990). Cerca con Google

[9] W. Kurz and D.J. Fisher: 'Fundamentals of solidification', 4th ed., pp.305; Switzerland, Trans Tech Publications, (1998). Cerca con Google

[10] Standard EN 1706:2010, 'Aluminium and aluminium alloys - Castings - Chemical composition and mechanical properties', (2010). Cerca con Google

[11] J.A.S. Green: 'Aluminum Recycling and Processing for Energy Conservation and Sustainability', USA, ASM International, (2007). Cerca con Google

[12] P.N. Crepeau: 'Effect of Iron in AI-Si Casting Alloys: A Critical Review', AFS Trans., vol.103, pp.361-366, (1995). Cerca con Google

[13] ASSOFOND: Report on EU & Italian Foundry in 2011, Assofond, Milano, (2012). Cerca con Google

[14] Stacast: 1st Pubblic Meeting, Stacast project - New Quality and Design Standards for Aluminium Alloys Cast Products, Call FP7-NMP-2012-CSA-6, Project Number: 319188, Milano, (2013). Cerca con Google

[15] Standard EN 1676:2010, 'Aluminium and aluminium alloys - Alloyed ingots for remelting - Specifications', (2010). Cerca con Google

[16] J.L. Jorstad: Proc. of 12th Int. Summer School on 'Light Alloy Castings: from Innovative Design to Advanced Applications', Vicenza (IT), July 25th - 29th, (2011). Cerca con Google

[17] D. Apelian: Worldwide Report - Aluminum Cast Alloys: Enabling Tools for Improved Performance, NADCA, USA, (2009). Cerca con Google

[18] ASM: 'Handbook: Vol.15 Casting', 9th ed., pp.1256; USA, ASM International, (2002). Cerca con Google

[19] J. Campbell: 'Castings', 2nd ed., Great Britain, Butterworth-Heinemann, (2003). Cerca con Google

[20] C.M. Dinnis, J.A. Taylor, and A.K. Dahle: 'Iron-related porosity in Al–Si–(Cu) foundry alloys', Mater. Sci. Eng. A, vol.425(1-2), pp.286-296, (2006). Cerca con Google

[21] L. Lu and A.K. Dahle: 'Iron-rich intermetallic phases and their role in casting defect formation in hypoeutectic Al−Si alloys', Metall. Mater. Trans. A, vol.36(13), pp.819-835, (2005). Cerca con Google

[22] A.M.A. Mohamed, A.M. Samuel, F.H. Samuel, and H.W. Doty: 'Influence of additives on the microstructure and tensile properties of near-eutectic Al–10.8%Si cast alloy', Mater. Design, vol.30(10), pp.3943-3957, (2009). Cerca con Google

[23] A.M.A. Mohamed, F.H. Samuel, A.M. Samuel, and H.W. Doty: 'Influence of additives on the impact toughness of Al–10.8% Si near-eutectic cast alloys', Mater. Design, vol.30(10), pp.4218-4229, (2009). Cerca con Google

[24] S. Seifeddine and I.L. Svensson: 'The influence of Fe and Mn content and cooling rate on the microstructure and mechanical properties of A380-die casting alloys', Metall. Sci. Technol., vol.27(1), pp.11-20, (2009). Cerca con Google

[25] S.G. Shabestari: 'The effect of iron and manganese on the formation of intermetallic compounds in aluminum–silicon alloys', Mater. Sci. Eng. A, vol.383(2), pp.289-298, (2004). Cerca con Google

[26] M.M. Makhlouf and D. Apelian: 'Casting characteristics of aluminum die casting alloys', Work Performed Under DOE Contract No. DEFC07-99ID13716, vol., pp.1-46, (2002). Cerca con Google

[27] S. Shankar and D. Apelian: 'Die soldering: Mechanism of the interface reaction between molten aluminum alloy and tool steel', Metall. Mater. Trans. B, vol.33(3), pp.465-476, (2002). Cerca con Google

[28] J.L. Jorstad: 'Understanding Sludge', Die Casting Engineer, vol., pp.30-36, (1986). Cerca con Google

[29] G. Gustafsson, T. Thorvaldsson, and G.L. Dunlop: 'The influence of Fe and Cr on the microstructure of cast Al-Si-Mg alloys', Metall. Trans. A, vol.17(1), pp.45-52, (1986). Cerca con Google

[30] L.F. Mondolfo: 'Aluminium alloys : structure and properties', Butterworths, (1976). Cerca con Google

[31] G. Timelli and F. Bonollo: 'The influence of Cr content on the microstructure and mechanical properties of AlSi9Cu3(Fe) die-casting alloys', Mater. Sci. Eng. A, vol.528(1), pp.273-282, (2010). Cerca con Google

[32] G. Timelli and F. Bonollo: 'Influence of tin and bismuth on machinability of lead free 6000 series aluminium alloys', Mater. Sci. Tech., vol.27(1), pp.291-299, (2011). Cerca con Google

[33] D.E.J. Talbot and C.E. Ransley: 'The addition of bismuth to aluminum-magnesium alloys to prevent embrittlement by sodium', Metall. Trans. A, vol.8(7), pp.1149-1154, (1977). Cerca con Google

[34] G. Timelli, G. Camicia, and S. Ferraro: 'Effect of Grain Refinement and Cooling Rate on the Microstructure and Mechanical Properties of Secondary Al-Si-Cu Alloys', J. Mater. Eng. Perform., vol., pp.1-11, (2013). Cerca con Google

[35] P. Schumacher, A.L. Greer, J. Worth, P.V. Evans, M.A. Kearns, P. Fisher, and A.H. Green: 'New studies of nucleation mechanisms in aluminium alloys: implications for grain refinement practice', Mater. Sci. Tech., vol.14(5), pp.394-404, (1998). Cerca con Google

[36] A.L. Greer, P.S. Cooper, M.W. Meredith, W. Schneider, P. Schumacher, J.A. Spittle, and A. Tronche: 'Grain Refinement of Aluminium Alloys by Inoculation', Adv. Eng. Mater., vol.5(1-2), pp.81-91, (2003). Cerca con Google

[37] M. Easton and D. StJohn: 'Grain refinement of aluminum alloys: Part I. the nucleant and solute paradigms—a review of the literature', Metall. Mater. Trans. A, vol.30(6), pp.1613-1623, (1999). Cerca con Google

[38] M. Easton and D. StJohn: 'Grain refinement of aluminum alloys: Part II. Confirmation of, and a mechanism for, the solute paradigm', Metall. Mater. Trans. A, vol.30(6), pp.1625-1633, (1999). Cerca con Google

[39] A.K. Dahle: Proc. of 12th Int. Summer School on 'Light Alloy Castings: from Innovative Design to Advanced Applications', Vicenza (IT), July 25th - 29th, (2011). Cerca con Google

[40] D. Apelian and J.L. Jorstad: 'Pressure Assisted Processes for High Integrity Automotive Aluminum Castings - Part 1: Principles and Fundamentals', 3rd Int. conference High Tech Die Casting, Vicenza (IT), 21-22 September, (2006). Cerca con Google

[41] E.J. Vinarcik: 'High Integrity Die Casting Processes', pp.223; USA, Wiley, (2002). Cerca con Google

[42] J.R. Brown: 'Foseco Non-Ferrous Foundryman's Handbook', 11th ed., pp.304; Oxford, Butterworth-Heinemann, (1999). Cerca con Google

[43] J. Campbell: 'Complete Casting Handbook: Metal Casting Processes, Metallurgy, Techniques and Design', pp.1220; UK, Elsevier Butterworth-Heinemann, (2011). Cerca con Google

[44] G. Timelli, S. Ferraro, F. Grosselle, F. Bonollo, F. Voltazza, and L. Capra: 'Caratterizzazione meccanica e microstrutturale di leghe di alluminio pressocolate', La Metallurgia Italiana, vol.101(1), pp.5-17, (2011). Cerca con Google

[45] H.I. Laukli: 'High Pressure Die Casting of Aluminium and Magnesium Alloys - Grain Structure and Segregation Characteristics', PhD thesis, Norwegian University of Science and Technology (NTNU), Trondheim, (2004). Cerca con Google

[46] E. Gariboldi, F. Bonollo, and P. Parona: 'Handbook of defects in high pressure diecastings', pp.132; Milano (IT), AIM, (2010). Cerca con Google

[47] EU: 'Directive 2000/53/EC- End of Life Vehicles', Official Journal of the European Communities, vol.L269, pp.34-42, (2000). Cerca con Google

[48] EU: 'Directive 2011/65/EU - On the restriction of the use of certain hazardous substances in electrical and electronic equipment', Official Journal of the European Communities, vol.L174, pp.88-110, (2011). Cerca con Google

[49] S. Capuzzi: 'Sviluppo di trattamenti termici per componenti automotive colati in lega di alluminio secondario allo stato semi-solido', MS thesis, University of Padova, Department of Menagement and Engineering (2012). Cerca con Google

[50] S. Ferraro, G. Timelli, and A. Fabrizi: 'Effects of Bismuth on the microstructure and mechanical properties of AlSi9Cu3(Fe) diecasting alloys', Mater. Sci. Forum, vol.765, pp.59-63, (2013). Cerca con Google

[51] G. Timelli, S. Ferraro, and A. Fabrizi: 'Effects of chromium and bismuth on secondary aluminium foundry alloys', Int. J. Cast. Met. Res., vol.26(4), pp.239-246, (2013). Cerca con Google

[52] A.J. McAlister: 'The Al−Bi (Aluminum−Bismuth) system', Bulletin of Alloy Phase Diagrams, vol.5(3), pp.247-250, (1984). Cerca con Google

[53] P.L. Schaffer, R.H. Mathiesen, L. Arnberg, M. Di Sabatino, and A. Snigirev: 'In situ investigation of spinodal decomposition in hypermonotectic Al–Bi and Al–Bi–Zn alloys', New Journal of Physics, vol.10(5), (2008). Cerca con Google

[54] A.A. Nayeb-Hashemi and J.B. Clark: 'The Bi-Mg (Bismuth-Magnesium) system', Bulletin of Alloy Phase Diagrams, vol.6(6), pp.528-533, (1985). Cerca con Google

[55] N.A. Gokcen: 'The Bi-Pb (Bismuth-Lead) system', JPE, vol.13(1), pp.21-32, (1992). Cerca con Google

[56] R.M. Pillai and T.R. Anantharaman: 'Elements of V Group as Modifiers of Aluminum-Silicon Alloys', Trans. Metall. AIME, vol.24(2), pp.2025-2027, (1968). Cerca con Google

[57] S. Farahany, A. Ourdjini, M.H. Idris, and L.T. Thai: 'Effect of bismuth on microstructure of unmodified and Sr-modified Al-7Si-0.4Mg alloys', Trans. Nonferr. Metal. soc., vol.21(7), pp.1455-1464, (2011). Cerca con Google

[58] J.I. Cho and C.R. Loper: 'Limitation of Bismuth Residual in A356.2 Aluminum', AFS Trans., vol.108, pp.359-367, (2000). Cerca con Google

[59] C.J. Machovec, J.W. Zindel, L.A. Godlewski, and G.E. Byczynski: 'Determining The Effect Of Bi-Sr Interactions On Si Morphology In 319Al', Modern Casting, vol.90(6), pp.42-44, (2000). Cerca con Google

[60] A. Papworth and P. Fox: 'The disruption of oxide defects within aluminium alloy castings by the addition of bismuth', Mater. Lett., vol.35(3–4), pp.202-206, (1998). Cerca con Google

[61] J. Shouxun, Y. Wenchao, G. Feng, W. Douglas, and F. Zhongyun: 'Effect of iron on the microstructure and mechanical property of Al–Mg–Si–Mn and Al–Mg–Si diecast alloys', Mater. Sci. Eng. A, vol.564, pp.130-139, (2012). Cerca con Google

[62] S. Ferraro and G. Timelli: 'Influence of Sludge Particles on the Tensile Properties of Die-cast Secondary Aluminium Alloys', Submitted for pubblication in: Mat. Sci. Eng. A, vol., (2013). Cerca con Google

[63] S. Seifeddine, S. Johansson, and I.L. Svensson: 'The influence of cooling rate and manganese content on the β-Al5FeSi phase formation and mechanical properties of Al–Si-based alloys', Mater. Sci. Eng. A, vol.490(1-2), pp.385-390, (2008). Cerca con Google

[64] J.A. Taylor, G.B. Schaffer, and D.H. StJohn: 'The role of iron in the formation of porosity in Al-Si-Cu-based casting alloys: Part I. Initial experimental observations', Metall. Mater. Trans. A, vol.30(6), pp.1643-1650, (1999). Cerca con Google

[65] ASM: 'Handbook: Vol.2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials', pp.1328; USA, ASM International, (2002). Cerca con Google

[66] L.A. Narayanan, F.H. Samuel, and J.E. Gruzleski: 'Crystallization behavior of iron-containing intermetallic compounds in 319 aluminum alloy', Metall. Mater. Trans. A, vol.25(8), pp.1761-1773, (1994). Cerca con Google

[67] G. Effenberg, H. Landolt, and S. Ilyenko: 'Ternary Alloy Systems: Phase Diagrams, Crystallographic and Thermodynamic Data', pp.292; Springer, (2008). Cerca con Google

[68] A. Fabrizi, S. Ferraro, and G. Timelli: 'The influence of Fe, Mn and Cr additions on the formation of Iron-rich intermetallic phases in an Al-Si die-casting alloy', Shape Casting 5: International Symposium, TMS, vol., (2014). Cerca con Google

[69] S. Ferraro, A. Fabrizi, and G. Timelli: 'The influence of Fe, Mn and Cr addition on Sludge in Die-cast Secondary Aluminum Alloys', Submitted for pubblication in: Metall. Mater. Trans. A, vol., (2013). Cerca con Google

[70] M. Warmuzek, W. Ratuszek, and G. Sęk-Sas: 'Chemical inhomogeneity of intermetallic phases precipitates formed during solidification of Al-Si alloys', Mater. Charact., vol.54(1), pp.31-40, (2005). Cerca con Google

[71] X. Cao, N. Saunders, and J. Campbell: 'Effect of iron and manganese contents on convection-free precipitation and sedimentation of primary α-Al(FeMn)Si phase in liquid Al-11.5Si-0.4Mg alloy', J. Mater. Sci., vol.39, pp.2303-2314, (2004). Cerca con Google

[72] S.G. Shabestari and J.E. Gruzleski: 'Gravity Segregation of Complex Intermetallic Compounds in Liquid Aluminum-Silicon Alloys ', Metall. Mater. Trans. A, vol.26A, pp.999-1006, (1995). Cerca con Google

[73] J. Gobrecht: 'Schwere seigerungen von Eisen, Mangan und Chrom in Aluminium-Silicium-Gußlegierungen ', Giesserei, vol.62(10), pp.263-266, (1975). Cerca con Google

[74] X. Cao and J. Campbell: 'Effect of Precipitation of Primary Intermetallic Compounds on the Mechanical Properties of Cast Al 11.5Si 0.4Mg Alloy', AFS Trans., vol.108, pp.391-400, (2000). Cerca con Google

[75] H.Y. Kim, S.W. Han, and H.M. Lee: 'The influence of Mn and Cr on the tensile properties of A356–0.20Fe alloy', Mater. Lett., vol.60(15), pp.1880-1883, (2006). Cerca con Google

[76] L. Ceschini, I. Boromei, A. Morri, S. Seifeddine, and I.L. Svensson: 'Microstructure, tensile and fatigue properties of the Al–10%Si–2%Cu alloy with different Fe and Mn content cast under controlled conditions', J. Mater. Process. Technol., vol.209(15-16), pp.5669-5679, (2009). Cerca con Google

[77] E. Taghaddos, M.M. Hejazi, R. Taghiabadi, and S.G. Shabestari: 'Effect of iron-intermetallics on the fluidity of 413 aluminum alloy', J. Alloys Compd., vol.468(1-2), pp.539-545, (2009). Cerca con Google

[78] W.H. Glaisher: 'Segregation of Iron and Manganese in Some Aluminium Casting Alloys', Metallurgia, vol., pp.127-131, (1951). Cerca con Google

[79] A. Kaye and A. Street: 'Chapter 8 - Inclusions and hard spots in aluminium alloys', in 'Die Casting Metallurgy', (eds. A. Kaye, et al.), pp.71-79; (1982), Butterworth-Heinemann. Cerca con Google

[80] R. Dunn: 'Aluminum Melting Problems and Their Influence on Furnace Selection', Die Casting Engineer, vol., pp.8-30, (1965). Cerca con Google

[81] X. Cao and J. Campbell: 'The nucleation of Fe-Rich phases on oxide films in Al-11.5Si-0.4Mg cast alloys', Metall. Mater. Trans. A, vol.34A, pp.1409-1420, (2003). Cerca con Google

[82] X. Cao: 'Heat Treatment of Liquid Metal - Precipitation and Sedimentation Processing of Liquid Al-11.5Si-0.4Mg Alloy', PhD thesis, University of Birmingham, School of Metallurgy and Materials, (2001). Cerca con Google

[83] X. Cao and J. Campbell: 'Effect of melt superheating on convection-free precipitation and sedimentation of primary α-Fe phase in liquid Al-11.5Si-0.4Mg alloy', Int. J. Cast. Met. Res., vol.15, pp.595-608, (2003). Cerca con Google

[84] X. Cao and J. Campbell: 'The Solidification Characteristics of Fe-Rich Intermetallics in Al-11.5Si-0.4Mg Cast Alloys', Mater. Sci. Eng. A, vol.35A, pp.1425-1435, (2004). Cerca con Google

[85] W. Khalifa, F.H. Samuel, J.E. Gruzleski, H.W. Doty, and S. Valtierra: 'Nucleation of Fe-Intermetallic Phases in the Al-Si-Fe Alloys', Metall. Mater. Trans. A, vol.36A, pp.1017-1032, (2005). Cerca con Google

[86] S. Terzi, J.A. Taylor, Y.H. Cho, L. Salvo, M. Suéry, E. Boller, and A.K. Dahle: 'In situ study of nucleation and growth of the irregular α-Al/β-Al5FeSi eutectic by 3-D synchrotron X-ray microtomography', Acta Mater., vol.58(16), pp.5370-5380, (2010). Cerca con Google

[87] A.M. Samuel, F.H. Samuel, H.W. Doty, and S. Valtierra: 'Effect of Superheat, Cooling Rate and Impurities on the Formation of Iron Intermetallics in Al-Si Die Casting Alloys ', AFS Trans., vol.109, pp.679-696, (2001). Cerca con Google

[88] S. Seifeddine and I.L. Svensson: 'Prediction of mechanical properties of cast aluminium components at various iron contents', Mater. Design, vol.31, pp.S6-S12, (2010). Cerca con Google

[89] J.Y. Hwang, H.W. Doty, and M.J. Kaufman: 'The effects of Mn additions on the microstructure and mechanical properties of Al–Si–Cu casting alloys', Mater. Sci. Eng. A, vol.488(1–2), pp.496-504, (2008). Cerca con Google

[90] Z. Ma, A.M. Samuel, F.H. Samuel, H.W. Doty, and S. Valtierra: 'A study of tensile properties in Al–Si–Cu and Al–Si–Mg alloys: Effect of β-iron intermetallics and porosity', Mater. Sci. Eng. A, vol.490(1-2), pp.36-51, (2008). Cerca con Google

[91] P. Beeley: 'Foundry Technology, 2nd Edition', pp.719; Oxford, United Kingdom, Butterworth-Heinemann, (2001). Cerca con Google

Download statistics

Solo per lo Staff dell Archivio: Modifica questo record