Reeder, Askia Enrico (2014) STUDY OF THE STRUCTURE AND THE ELECTRONIC PROPERTIES OF THE OXIDE/OXIDE INTERFACES IN MIXED METAL OXIDES. [Tesi di dottorato]

Full text disponibile come:

[img]
Anteprima
Documento PDF (STUDY OF THE STRUCTURE AND THE ELECTRONIC PROPERTIES OF THE OXIDE/OXIDE INTERFACES IN MIXED METAL OXIDES) - Versione accettata
11Mb

Abstract (inglese)

A very important role is played by metal oxides in many areas of chemistry, physics, and materials science. Transition metal and rare-earth metal elements are able to form a large diversity of oxide compounds which can adopt an ample array of atomic structures and electronic properties that can exhibit metallic, semiconductor, or insulator characteristics. In technological applications, metal oxides are used in the fabrication of microelectronic components, sensors, fuel cells, coatings to protect surfaces against corrosion, and as catalysts. In this thesis we have decided to study two known catalytic materials Zirconia-Titania and Ceria-Titania mixed oxides. For both materials bibliography principally concerns powders thus in order to better study their interfaces, of which a deeper study is still lacking, we decided to deposit zirconia and ceria as thin films onto rutile TiO2(110).
We first studied the zirconia-titania system by depositing an ultra-thin film of zirconium oxide via a metal-organic precursor: Zirconium Tetra tert-Butoxide. The deposition was carried at three different substrate temperatures 677 K, 738 K, 773 K in five stages of a minute each and the results were traced by using XPS. The chemical characterization via XPS showed an interesting chemistry undergoing on the substrate’s surface and we have observed the formation of carbonaceous species at the interface. Zirconium appeared to be at its highest oxidation state while titanium was seen to undergo reduction with each successive deposited layer. The ratio of the Zr/Ti signals showed that zirconia didn’t completely wet the surface. Furthermore, no long range order was observed via LEED. XPD measurements showed that zirconia does not form a substitutional oxide with titania. However with the aid of computer simulation we deduced that very likely zirconia forms nanochains on the surface of TiO2(110). This surface was exposed to 100 L of pyridine to test its acidity.
In the case of ceria, we have deposited the oxide on a heated TiO2(110) substrate via metal evaporation from a Mo crucible since the process is rather easy and garners clean deposits. During deposition the substrate was kept at 677 K and in an O2 environment of 5.2•10-6mbar, and, in order to obtain an ordered homogeneous surface the sample was further annealed in the same environment at 900 K. Through LEED imaging different phases were observed and were dependent on sample history and film thickness. Via computer simulation these phases were then referred to the parent oxide in order to better comprehend the difference in respect to the bulk phase. All films showed cerium present at Ce(III). Ultra-violet Photoelectron Spectroscopy showed the electronic properties of the film showing a binding energy shift and the population of Ce4f states due to stabilization of Ce(III) by TiO2(110). The reactivity of the ceria-titania system was the probed by using methanol and ethanol. Results showed that the addition of ceria opened the dehydrogenation path from alcohol to aldehyde. We have observed that oxygen pre-oxidation of the CeOx-TiO2(110) system had an impact on its selectivity by opening also a dehydration path from methanol and ethanol to respectively, methane and ethylene. This alternative path was viable only for low cerium oxide coverages as interaction with the substrate was needed for dehydration to occur. Aldehyde formation was seen to occur at mild temperatures (330 K) and was independent of film thickness. Subsequently, ceria-titania mixed oxide powders were characterized via XPS and we have observed that for increasing amount of cerium the element gradually became present at its highest oxidation state Ce(IV). By XPS we have also determined the formation of a very intimate composite between the two oxides by observing the increasing the full width at half maximum of the Ti2p peak for increasing amounts of cerium. Furthermore, compositional calculation showed that cerium had the tendency to disperse within the titania particles. These data helped to uncover a possibly good recipe for the formation of cerium titanate a composite with good oxygen storage capacity.

Abstract (italiano)

Un ruolo molto importante è svolto dagli ossidi metallici in molti settori della chimica, fisica e scienza dei materiali. I metalli di transizione e le terre rare sono in grado di formare una grande diversità di composti ossidici che possono adottare un'ampia gamma di strutture atomiche ed proprieta’ elettroniche che possono esibire caratteristiche metalliche, semiconduttrici o isolanti. In applicazioni tecnologiche, gli ossidi metallici sono impiegati nella fabbricazione di componenti microelettronici, sensori, celle a combustibile, rivestimenti per proteggere le superfici dalla corrosione, e come catalizzatori. In questa tesi abbiamo deciso di studiare due noti materiali catalitici: gli ossidi misti di Zirconia-Titania Ceria-Titania. Per entrambi i materiali la bibliografia riguarda principalmente le polveri quindi, al fine di studiare meglio le loro interfacce, di cui uno studio più approfondito e’ tuttora neccessario, abbiamo deciso di depositare film sottili di ossido di zirconio e ossido di cerio su rutilo TiO2(110).
Abbiamo prima studiato il sistema zirconia-titania depositando un film ultra-sottile di ossido di zirconio mediante un precursore metallo-organico: Zirconio Tetra tert-butossido. La deposizione è stata effettuata a tre diverse temperature del substrato 677. K, 738 K, 773 K in cinque fasi di un minuto ciascuno. La caratterizzazione mediante XPS ha mostrato una chimica interessante sulla superficie del substrato e abbiamo osservato la formazione di specie carboniose all'interfaccia. Lo zirconio sembrava essere nel suo piu’ alto stato di ossidazione mentre il titanio è stato visto gradualmente ridursi con ogni successive strato di deposito. Il rapporto dei segnali Zr/Ti ha mostrato che la zirconia non ha completamente coperto la superficie. Inoltre,tramite LEED non si e’ osservato nessun ordine a lungo raggio. Misure XPD ha mostrato che la zirconia non forma un ossido di sostituzione con la titania. Tuttavia, con l'ausilio di simulazione al computer abbiamo dedotto che la zirconia forma, molto probabilmente nanocatene sulla superficie di TiO2(110). Questa superficie è stato esposta a 100 L di pyridinina per testarne la acidita’.
Nel caso di ceria, abbiamo depositato l'ossido su un substrato riscaldato di TiO2 (110) tramite evaporazione del metallo da un crogiolo Mo poiché il processo è piuttosto facile e fornisce depositi puliti. Durante la deposizione il substrato è stata mantenuto a 677 K in un ambiente di 5,2 • 10 -6 mbar di O2, e, al fine di ottenere una superficie omogenea e ordinata il campione è stato ulteriormente sottoposto a trattamento termico nello stesso ambiente a 900 K. Tramite la tecnica LEED sono state osservate differenti fasi dipendenti dalla storia del campione e dallo spessore del film. Tramite simulazione al computer queste fasi sono stati poi riferite rispetto al biossido di cerio per meglio comprendere le differenze rispetto alla fase massiva. Tutti i film hanno mostrato cerio presenti come Ce(III). La Spettroscopia Fotoelettronica a Ultravioletti ha mostrato le proprietà elettroniche del film che mostra uno spostamento in energia di legame e un popolamento degli stati Ce4f. Questo e’ dovuto alla stabilizzazione di Ce (III) da parte di TiO2 (110). Si e’ volute osservare la reattività del sistema ceria-titania nei confronti di metanolo ed etanolo. I risultati hanno mostrato che l'aggiunta di ceria ha aperto il percorso della deidrogenazione degli alcoli ad aldeidi. Abbiamo osservato che la pre-ossidazione con ossigeno del sistema CeOx-TiO2(110) ha avuto un impatto sulla sua selettività aprendo anche un percorso di disidratazione di metanolo ed etanolo rispettivamente a metano ed etilene. Questa via alternativa era valida solo per basse coperture di ossido di cerio avendo osservato che l’interazione con il substrato è stato necessario perche’ avvenga la disidratazione. La formazione di aldeidi fu osservata avvenire a temperature piuttosto (330 K) ed essere indipendente dallo spessore del film. Successivamente sono state caratterizzate tramite XPS delle polveri di ossidi misti di ceria e titania. Abbiamo osservato che per quantità crescenti di cerio l'elemento diventa gradualmente sempre piu’ presente al suo stato di ossidazione più alto Ce (IV). Con XPS abbiamo anche determinato la formazione di un composito molto intimo tra i due ossidi osservando l'aumento della larghezza a metà altezza del picco Ti2p per quantità crescenti di cerio. Inoltre, la determinazione della composizione ha mostrato che il cerio ha la tendenza di disperdersi all'interno delle particelle di titania. Questi dati hanno contribuito a scoprire una possibile buona ricetta per la formazione di cerio titanato; un composito con buona capacità di stoccaggio di ossigeno.

Statistiche Download - Aggiungi a RefWorks
Tipo di EPrint:Tesi di dottorato
Relatore:Granozzi, Gaetano
Dottorato (corsi e scuole):Ciclo 25 > Scuole 25 > SCIENZA ED INGEGNERIA DEI MATERIALI
Data di deposito della tesi:30 Gennaio 2014
Anno di Pubblicazione:30 Gennaio 2014
Parole chiave (italiano / inglese):STRUCTURE ELECTRONIC PROPERTIES OXIDE INTERFACES MIXED METAL METHANOL ETHANOL TPD PHASES CERIA ZIRCONIA TITANIA
Settori scientifico-disciplinari MIUR:Area 03 - Scienze chimiche > CHIM/02 Chimica fisica
Area 03 - Scienze chimiche > CHIM/07 Fondamenti chimici delle tecnologie
Area 03 - Scienze chimiche > CHIM/03 Chimica generale e inorganica
Struttura di riferimento:Dipartimenti > Dipartimento di Scienze Chimiche
Codice ID:6800
Depositato il:24 Apr 2015 16:10
Simple Metadata
Full Metadata
EndNote Format

Bibliografia

I riferimenti della bibliografia possono essere cercati con Cerca la citazione di AIRE, copiando il titolo dell'articolo (o del libro) e la rivista (se presente) nei campi appositi di "Cerca la Citazione di AIRE".
Le url contenute in alcuni riferimenti sono raggiungibili cliccando sul link alla fine della citazione (Vai!) e tramite Google (Ricerca con Google). Il risultato dipende dalla formattazione della citazione.

1. H. Y. Hwang, Y. Iwasa, M. Kawasaki, B. Keimer, N. Nagaosa and Y. Tokura, Nat Mater, 2012, 11, 103-113. Cerca con Google

2. J. N. Armor, Catal Today, 2011, 163, 3-9. Cerca con Google

3. G. Centi and S. Perathoner, Catal Today, 2008, 138, 69-76. Cerca con Google

4. A. Alves, F. Berutti and F. Sánchez, in Nanostructured Materials for Engineering Applications, eds. C. Bergmann and M. Andrade, Springer Berlin Heidelberg, Editon edn., 2011, pp. 93-117. Cerca con Google

5. A. Filho and S. Fagan, in Nanostructured Materials for Engineering Applications, eds. C. Bergmann and M. Andrade, Springer Berlin Heidelberg, Editon edn., 2011, pp. 5-22. Cerca con Google

6. U. Diebold, Surface Science Reports, 2003, 48, 53-229. Cerca con Google

7. C. L. Pang, R. Lindsay and G. Thornton, Chem Soc Rev, 2008, 37, 2328-2353. Cerca con Google

8. Y. Han and J. Zhu, Top Catal, 2013, 56, 1525-1541. Cerca con Google

9. B. Kaemena, S. D. Senanayake, A. Meyer, J. T. Sadowski, J. Falta and J. I. Flege, The Journal of Physical Chemistry C, 2012, 117, 221-232. Cerca con Google

10. M. J. Muñoz-Batista, M. N. Gómez-Cerezo, A. Kubacka, D. Tudela and M. Fernández-García, Acs Catal, 2013, 4, 63-72. Cerca con Google

11. A. Kitiyanan, S. Sakulkhaemaruethai, Y. Suzuki and S. Yoshikawa, Compos Sci Technol, 2006, 66, 1259-1265. Cerca con Google

12. J. B. Park, J. Graciani, J. Evans, D. Stacchiola, S. Ma, P. Liu, A. Nambu, J. Fernandez Sanz, J. Hrbek and J. A. Rodriguez, Proceedings of the National Academy of Sciences of the United States of America, 2009, 106, 4975-4980. Cerca con Google

13. G. A. Olah, Angewandte Chemie International Edition, 2005, 44, 2636-2639. Cerca con Google

14. M. Ni, D. Y. C. Leung and M. K. H. Leung, Int J Hydrogen Energ, 2007, 32, 3238-3247. Cerca con Google

15. V. Subramani and C. Song, in Catalysis: Volume 20, The Royal Society of Chemistry, Editon edn., 2007, vol. 20, pp. 65-106. Cerca con Google

16. W. M. LC Feldman, Fundamentals of Surface and Thin Film Analysis, 1986, Elsevier. Cerca con Google

17. M. S. D. Briggs, Practical Surface Analysis, Second Edition, Volume 1, Auger and X-Ray Photoelectron Spectroscopy 1990, Wiley. Cerca con Google

18. C. R. B. C S Fadley, A D Baker, Basic Concepts of X-ray Photoelectron Spectroscopy, in Electron Spectroscopy, Theory, and Thechniques Apllications, 1978, Pergamon Press. Cerca con Google

19. M. Eusebio, University of Padua, 2003. Cerca con Google

20. S. Tanuma, C. J. Powell and D. R. Penn, Surface and Interface Analysis, 1988, 11, 577-589. Cerca con Google

21. S. Tanuma, C. J. Powell and D. R. Penn, Surface and Interface Analysis, 1991, 17, 911-926. Cerca con Google

22. S. Tanuma, C. J. Powell and D. R. Penn, Surface and Interface Analysis, 1991, 17, 927-939. Cerca con Google

23. S. Tanuma, C. J. Powell and D. R. Penn, Surface and Interface Analysis, 1993, 20, 77-89. Cerca con Google

24. S. Tanuma, C. J. Powell and D. R. Penn, Surface and Interface Analysis, 2003, 35, 268-275. Cerca con Google

25. S. Tanuma, C. J. Powell and D. R. Penn, Surface and Interface Analysis, 2005, 37, 1-14. Cerca con Google

26. N. Beatham and A. F. Orchard, Journal of Electron Spectroscopy and Related Phenomena, 1979, 16, 77-86. Cerca con Google

27. B. L. Henke, Physical Review A, 1972, 6, 94-104. Cerca con Google

28. M. Mehta and C. S. Fadley, Physics Letters A, 1975, 55, 59-61. Cerca con Google

29. G. Granozzi, Lecture notes of the course of Solid State Chemistry and Surfaces, 1999, Vol 2. Cerca con Google

30. www.matter.org.uk/diffraction/. Vai! Cerca con Google

31. P. Hofmann, Lecture Notes on Surface Science, 2005. Cerca con Google

32. http://capsicum.me.utexas.edu/ChE386K/. Vai! Cerca con Google

33. G. Granozzi, Lecture notes of the course of Solid State Chemistry and Surfaces, 1999, Vol 6. Cerca con Google

34. M. G. S L M Schroeder, Lecture Notes - Advanced Physical Chemistry Laboratory, 2002, FU Berlin. Cerca con Google

35. J. A. W. Elliott and C. A. Ward, The Journal of Chemical Physics, 1997, 106, 5677-5684. Cerca con Google

36. D. K. Chakrabarty and B. Viswanathan, Heterogeneous Catalysis, New Age Science, Limited, 2009. Cerca con Google

37. S. P. Jiang and S. H. Chan, J Mater Sci, 2004, 39, 4405-4439. Cerca con Google

38. P. W. Peacock and J. Robertson, Appl Phys Lett, 2003, 83, 2025-2027. Cerca con Google

39. M. Copel, M. Gribelyuk and E. Gusev, Appl Phys Lett, 2000, 76, 436-438. Cerca con Google

40. K. Tanabe and T. Yamaguchi, Catal Today, 1994, 20, 185-197. Cerca con Google

41. T. Yamaguchi, Catal Today, 1994, 20, 199-217. Cerca con Google

42. J. Fung and I. Wang, J Catal, 1996, 164, 166-172. Cerca con Google

43. T. C. Schilke, I. A. Fisher and A. T. Bell, J Catal, 1999, 184, 144-156. Cerca con Google

44. S. Yang, A. Maroto-Valiente, M. Benito-Gonzalez, I. Rodriguez-Ramos and A. Guerrero-Ruiz, Applied Catalysis B: Environmental, 2000, 28, 223-233. Cerca con Google

45. R. J. Farrauto and R. M. Heck, Catal Today, 1999, 51, 351-360. Cerca con Google

46. Y. Kohno, T. Tanaka, T. Funabiki and S. Yoshida, Phys Chem Chem Phys, 2000, 2, 5302-5307. Cerca con Google

47. A. Kitiyanan, S. Sakulkhaemaruethai, Y. Suzuki and S. Yoshikawa, Compos Sci Technol, 2006, 66, 1259-1265. Cerca con Google

48. Y. Paz, Applied Catalysis B: Environmental, 2010, 99, 448-460. Cerca con Google

49. B. O'Regan and M. Gratzel, Nature, 1991, 353, 737-740. Cerca con Google

50. R. H. French, S. J. Glass, F. S. Ohuchi, Y. N. Xu and W. Y. Ching, Phys Rev B, 1994, 49, 5133-5142. Cerca con Google

51. N. Siedl, M. J. Elser, J. Bernardi and O. Diwald, The Journal of Physical Chemistry C, 2009, 113, 15792-15795. Cerca con Google

52. H. Zou and Y. S. Lin, Applied Catalysis A: General, 2004, 265, 35-42. Cerca con Google

53. B. M. Reddy and A. Khan, Catalysis Reviews, 2005, 47, 257-296. Cerca con Google

54. L. Liang, Y. Sheng, Y. Xu, D. Wu and Y. Sun, Thin Solid Films, 2007, 515, 7765-7771. Cerca con Google

55. K. V. R. Chary, G. V. Sagar, D. Naresh, K. K. Seela and B. Sridhar, The Journal of Physical Chemistry B, 2005, 109, 9437-9444. Cerca con Google

56. S. Livraghi, F. Olivero, M. C. Paganini and E. Giamello, The Journal of Physical Chemistry C, 2010, 114, 18553-18558. Cerca con Google

57. B. Mitu, S. Vizireanu, R. Birjega, M. Dinescu, S. Somacescu, P. Osiceanu, V. Pârvulescu and G. Dinescu, Thin Solid Films, 2007, 515, 6484-6488. Cerca con Google

58. M. D. Hernández-Alonso, J. M. Coronado, B. Bachiller-Baeza, M. Fernández-García and J. Soria, Chem Mater, 2007, 19, 4283-4291. Cerca con Google

59. D. C. Bradley, Chem Rev, 1989, 89, 1317-1322. Cerca con Google

60. M. A. Cameron and S. M. George, Thin Solid Films, 1999, 348, 90-98. Cerca con Google

61. D. J. Burleson, J. T. Roberts, W. L. Gladfelter, S. A. Campbell and R. C. Smith, Chem Mater, 2002, 14, 1269-1276. Cerca con Google

62. K. Kukli, M. Ritala and M. Leskelä, Chem Vapor Depos, 2000, 6, 297-302. Cerca con Google

63. Y.-S. Lin, R. Puthenkovilakam, J. P. Chang, C. Bouldin, I. Levin, N. V. Nguyen, J. Ehrstein, Y. Sun, P. Pianetta, T. Conard, W. Vandervorst, V. Venturo and S. Selbrede, J Appl Phys, 2003, 93, 5945-5952. Cerca con Google

64. J. P. Chang, Y.-S. Lin and K. Chu, Journal of Vacuum Science Technology B, 2001, 19, 1782-1787. Cerca con Google

65. P. G. Karlsson, J. H. Richter, J. Blomquist, P. Uvdal, T. M. Grehk and A. Sandell, Surf Sci, 2007, 601, 1008-1018. Cerca con Google

66. P. G. Karlsson, E. Göthelid, J. H. Richter and A. Sandell, Surf Sci, 2008, 602, 1803-1809. Cerca con Google

67. B. H. Lee, S. Cho, J. K. Hwang, S. H. Kim and M. M. Sung, Thin Solid Films, 2010, 518, 6432-6436. Cerca con Google

68. D. Panda and T.-Y. Tseng, Thin Solid Films, 2013, 531, 1-20. Cerca con Google

69. K. F. McCarty, Surf Sci, 2003, 543, 185-206. Cerca con Google

70. M. Li, W. Hebenstreit, L. Gross, U. Diebold, M. A. Henderson, D. R. Jennison, P. A. Schultz and M. P. Sears, Surf Sci, 1999, 437, 173-190. Cerca con Google

71. G. Granozzi and M. Sambi, Adv Mater, 1996, 8, 315-326. Cerca con Google

72. F. J. G. de Abajo, M. A. Van Hove and C. S. Fadley, Physical Review B, 2001, 63. Cerca con Google

73. S. Harel, J. M. Mariot and C. F. Hague, Surf Sci, 1992, 269, 1167-1172. Cerca con Google

74. K. Sakamoto, H. M. Zhang and R. I. G. Uhrberg, Phys Rev B, 2003, 68, 075302. Cerca con Google

75. B. J. Gould, I. M. Povey, M. E. Pemble and W. R. Flavell, J Mater Chem, 1994, 4, 1815-1819. Cerca con Google

76. M. D. Robbins and M. A. Henderson, J Catal, 2006, 238, 111-121. Cerca con Google

77. S. T. Korhonen, M. Calatayud and A. O. I. Krause, The Journal of Physical Chemistry C, 2008, 112, 6469-6476. Cerca con Google

78. C. S. Fadley, Prog Surf Sci, 1984, 16, 275-388. Cerca con Google

79. G. A. Rizzi, A. E. Reeder, S. Agnoli and G. Granozzi, Surf Sci, 2006, 600, 3345-3351. Cerca con Google

80. L. Artiglia, S. Agnoli, A. Vittadini, A. Verdini, A. Cossaro, L. Floreano and G. Granozzi, J Am Chem Soc, 2013, 135, 17331-17338. Cerca con Google

81. F. Yang, S. Kundu, A. B. Vidal, J. Graciani, P. J. Ramírez, S. D. Senanayake, D. Stacchiola, J. Evans, P. Liu, J. F. Sanz and J. A. Rodriguez, Angewandte Chemie International Edition, 2011, 50, 10198-10202. Cerca con Google

82. S. X. Luo, F. M. Wang, Z. S. Shi and F. Xin, Mater Res Innov, 2009, 13, 64-69. Cerca con Google

83. A. Paulidou and R. M. Nix, Phys Chem Chem Phys, 2005, 7, 1482-1489. Cerca con Google

84. A. Trunschke, D. L. Hoang, J. Radnik, K. W. Brzezinka, A. Brückner and H. Lieske, Applied Catalysis A: General, 2001, 208, 381-392. Cerca con Google

85. D. L. Hoang, H. Preiss, B. Parlitz, F. Krumeich and H. Lieske, Applied Catalysis A: General, 1999, 182, 385-397. Cerca con Google

86. U. Martinez, L. B. Vilhelmsen, H. H. Kristoffersen, J. Stausholm-Møller and B. Hammer, Phys Rev B, 2011, 84, 205434. Cerca con Google

87. U. Martinez, L. B. Vilhelmsen, H. H. Kristoffersen, J. Stausholm-Møller and B. Hammer, Phys Rev B, 2011, 84, 205434. Cerca con Google

88. A. Trovarelli, C. de Leitenburg, M. Boaro and G. Dolcetti, Catal Today, 1999, 50, 353-367. Cerca con Google

89. A. Trovarelli, Catalysis Reviews-Science and Engineering, 1996, 38, 439-520. Cerca con Google

90. J. Kašpar, P. Fornasiero and M. Graziani, Catal Today, 1999, 50, 285-298. Cerca con Google

91. S. Imamura and M. Ando, Ind Eng Chem Res, 1989, 28, 1452-1456. Cerca con Google

92. Q. Fu, A. Weber and M. Flytzani-Stephanopoulos, Catal Lett, 2001, 77, 87-95. Cerca con Google

93. Q. Fu, H. Saltsburg and M. Flytzani-Stephanopoulos, Science, 2003, 301, 935-938. Cerca con Google

94. P. Jasinski, T. Suzuki and H. U. Anderson, Sensors and Actuators B: Chemical, 2003, 95, 73-77. Cerca con Google

95. M. Stoukides, Catalysis Reviews, 2000, 42, 1-70. Cerca con Google

96. S. Park, J. M. Vohs and R. J. Gorte, Nature, 2000, 404, 265-267. Cerca con Google

97. S. Armini, J. De Messemaeker, C. M. Whelan, M. Moinpour and K. Maex, J Electrochem Soc, 2008, 155, H653-H660. Cerca con Google

98. A. Asati, S. Santra, C. Kaittanis, S. Nath and J. M. Perez, Angewandte Chemie International Edition, 2009, 48, 2308-2312. Cerca con Google

99. M. Mogensen, N. M. Sammes and G. A. Tompsett, Solid State Ionics, 2000, 129, 63-94. Cerca con Google

100. W. Xiao, Q. Guo and E. G. Wang, Chem Phys Lett, 2003, 368, 527-531. Cerca con Google

101. J. A. Kilner, Chem Lett, 2008, 37, 1012-1015. Cerca con Google

102. C. T. Campbell and C. H. F. Peden, Science, 2005, 309, 713-714. Cerca con Google

103. C. Sun, H. Li and L. Chen, Energ Environ Sci, 2012, 5, 8475-8505. Cerca con Google

104. S. Tsunekawa, R. Sahara, Y. Kawazoe and K. Ishikawa, Appl Surf Sci, 1999, 152, 53-56. Cerca con Google

105. S. Deshpande, S. Patil, S. V. Kuchibhatla and S. Seal, Appl Phys Lett, 2005, 87, -. Cerca con Google

106. T. Yu, J. Joo, Y. I. Park and T. Hyeon, Angewandte Chemie International Edition, 2005, 44, 7411-7414. Cerca con Google

107. D. Wang, Y. Kang, V. Doan-Nguyen, J. Chen, R. Küngas, N. L. Wieder, K. Bakhmutsky, R. J. Gorte and C. B. Murray, Angewandte Chemie, 2011, 123, 4470-4473. Cerca con Google

108. S. T. Bromley, I. d. P. R. Moreira, K. M. Neyman and F. Illas, Chem Soc Rev, 2009, 38, 2657-2670. Cerca con Google

109. J. Rynkowski, J. Farbotko, R. Touroude and L. Hilaire, Applied Catalysis A: General, 2000, 203, 335-348. Cerca con Google

110. B. Reddy and A. Khan, Catal Surv Asia, 2005, 9, 155-171. Cerca con Google

111. G. Dutta, U. V. Waghmare, T. Baidya, M. S. Hegde, K. R. Priolkar and P. R. Sarode, Chem Mater, 2006, 18, 3249-3256. Cerca con Google

112. J. Fang, H. Bao, B. He, F. Wang, D. Si, Z. Jiang, Z. Pan, S. Wei and W. Huang, The Journal of Physical Chemistry C, 2007, 111, 19078-19085. Cerca con Google

113. G. Zhou, J. Hanson and R. J. Gorte, Applied Catalysis A: General, 2008, 335, 153-158. Cerca con Google

114. S. Watanabe, X. Ma and C. Song, The Journal of Physical Chemistry C, 2009, 113, 14249-14257. Cerca con Google

115. A. C. Johnston-Peck, S. D. Senanayake, J. J. Plata, S. Kundu, W. Xu, L. Barrio, J. Graciani, J. F. Sanz, R. M. Navarro, J. L. G. Fierro, E. A. Stach and J. A. Rodriguez, The Journal of Physical Chemistry C, 2013, 117, 14463-14471. Cerca con Google

116. T. Masui, K. Fukuhara, N. Imanaka, T. Sakata, H. Mori and G.-y. Adachi, Chem Lett, 2002, 31, 474-475. Cerca con Google

117. J. Xiao, X. Wang, Y. Chen, M. Fujii and C. Song, Ind Eng Chem Res, 2013, 52, 15746-15755. Cerca con Google

118. J. A. Rodriguez and D. Stacchiola, Phys Chem Chem Phys, 2010, 12, 9557-9565. Cerca con Google

119. A. Bruix, J. A. Rodriguez, P. J. Ramirez, S. D. Senanayake, J. Evans, J. B. Park, D. Stacchiola, P. Liu, J. Hrbek and F. Illas, J Am Chem Soc, 2012, 134, 8968-8974. Cerca con Google

120. L. V. Mattos and F. B. Noronha, J Catal, 2005, 233, 453-463. Cerca con Google

121. C. Xu, R. Zeng, P. K. Shen and Z. Wei, Electrochim Acta, 2005, 51, 1031-1035. Cerca con Google

122. G. Jacobs, R. A. Keogh and B. H. Davis, J Catal, 2007, 245, 326-337. Cerca con Google

123. J. B. Park, J. Graciani, J. Evans, D. Stacchiola, S. Ma, P. Liu, A. Nambu, J. Fernandez Sanz, J. Hrbek and J. A. Rodriguez, Proceedings of the National Academy of Sciences of the United States of America, 2009, 106, 4975-4980. Cerca con Google

124. J. B. Park, J. Graciani, J. Evans, D. Stacchiola, S. D. Senanayake, L. Barrio, P. Liu, J. F. Sanz, J. Hrbek and J. A. Rodriguez, J Am Chem Soc, 2010, 132, 356-363. Cerca con Google

125. P. Burroughs, A. Hamnett, A. F. Orchard and G. Thornton, Journal of the Chemical Society, Dalton Transactions, 1976, 1686-1698. Cerca con Google

126. A. Kotani, H. Mizuta, T. Jo and J. C. Parlebas, Solid State Commun, 1985, 53, 805-810. Cerca con Google

127. T. Jo and A. Kotani, Solid State Commun, 1985, 54, 451-456. Cerca con Google

128. R. Wrobel, Y. Suchorski, S. Becker and H. Weiss, Surf Sci, 2008, 602, 436-442. Cerca con Google

129. E. Beche, P. Charvin, D. Perarnau, S. Abanades and G. Flamant, Surf Interface Anal, 2008, 40, 264-267. Cerca con Google

130. A. Pfau and K. D. Schierbaum, Surf Sci, 1994, 321, 71-80. Cerca con Google

131. Y. A. Teterin, A. Y. Teterin, A. M. Lebedev and I. O. Utkin, Journal of Electron Spectroscopy and Related Phenomena, 1998, 88, 275-279. Cerca con Google

132. J. Graciani, J. J. Plata, J. Fdez Sanz, P. Liu and J. A. Rodriguez, J Chem Phys, 2010, 132. Cerca con Google

133. Y. Zhou and J. Zhou, Surf Sci, 2012, 606, 749-753. Cerca con Google

134. M. Fronzi, A. Soon, B. Delley, E. Traversa and C. Stampfl, J Chem Phys, 2009, 131. Cerca con Google

135. R. Wang, P. A. Crozier and R. Sharma, J Phys Chem C, 2009, 113, 5700-5704. Cerca con Google

136. X. Shao, J.-F. Jerratsch, N. Nilius and H.-J. Freund, Phys Chem Chem Phys, 2011, 13, 12646-12651. Cerca con Google

137. M. Nielsen, E. Alberico, W. Baumann, H.-J. Drexler, H. Junge, S. Gladiali and M. Beller, Nature, 2013, 495, 85-89. Cerca con Google

138. A. Haryanto, S. Fernando, N. Murali and S. Adhikari, Energ Fuel, 2005, 19, 2098-2106. Cerca con Google

139. V. Subramani and C. Song, in Catalysis: Volume 20, The Royal Society of Chemistry, Editon edn., 2007, vol. 20, pp. 65-106. Cerca con Google

140. G. A. Deluga, J. R. Salge, L. D. Schmidt and X. E. Verykios, Science, 2004, 303, 993-997. Cerca con Google

141. M. Ni, D. Y. C. Leung and M. K. H. Leung, Int J Hydrogen Energ, 2007, 32, 3238-3247. Cerca con Google

142. P. D. Vaidya and A. E. Rodrigues, Chem Eng J, 2006, 117, 39-49. Cerca con Google

143. U. Diebold, Surface Science Reports, 2003, 48, 53-229. Cerca con Google

144. C. L. Pang, R. Lindsay and G. Thornton, Chem Soc Rev, 2008, 37, 2328-2353. Cerca con Google

145. W. S. Epling, C. H. F. Peden, M. A. Henderson and U. Diebold, Surf Sci, 1998, 412–413, 333-343. Cerca con Google

146. W. S. Epling, C. H. F. Peden, M. A. Henderson and U. Diebold, Surf Sci, 1998, 412-13, 333-343. Cerca con Google

150. G. Lu, A. Linsebigler and J. T. Yates, The Journal of Physical Chemistry, 1994, 98, 11733-11738. Cerca con Google

151. L. Gamble, L. S. Jung and C. T. Campbell, Surf Sci, 1996, 348, 1-16. Cerca con Google

152. E. Farfan-Arribas and R. J. Madix, The Journal of Physical Chemistry B, 2002, 106, 10680-10692. Cerca con Google

153. M. A. Henderson, S. Otero-Tapia and M. E. Castro, Faraday Discuss, 1999, 114, 313-329. Cerca con Google

154. S. Wendt, P. T. Sprunger, E. Lira, G. K. H. Madsen, Z. Li, J. Ø. Hansen, J. Matthiesen, A. Blekinge-Rasmussen, E. Lægsgaard, B. Hammer and F. Besenbacher, Science, 2008, 320, 1755-1759. Cerca con Google

155. A. Siokou and R. M. Nix, J Phys Chem B, 1999, 103, 6984-6997. Cerca con Google

156. R. M. Ferrizz, G. S. Wong, T. Egami and J. M. Vohs, Langmuir, 2001, 17, 2464-2470. Cerca con Google

157. D. R. Mullins, S. D. Senanayake and T. L. Chen, The Journal of Physical Chemistry C, 2010, 114, 17112-17119. Cerca con Google

Download statistics

Solo per lo Staff dell Archivio: Modifica questo record