Crema, Luca (2016) A STUDY OF RAPID MOULD TEMPERATURE VARIATION INFLUENCE ON MORPHOLOGY AND APPEARANCE OF INJECTION MOULDED PARTS. [Tesi di dottorato]

Full text disponibile come:

[img]
Anteprima
Documento PDF
80Mb

Abstract (inglese)

Rapid Heating Cycle Molding (RHCM) is a widely used technology for manufacturing high gloss components without visible surface defects. Due to the several improvements such as the injection pressure reduction, the increasing on molded parts quality and the possibility to control the mold temperature, this technology is becoming an interesting solution for injection molding of thin wall components with engineering polymers. The elevated mold temperature, however, substantially increases the cycle time, thus lowering the productivity to a great extent. Development of capable techniques for rapidly heating and cooling a mold with a relatively large mass is technically challenging because of the constraints set by the injection molding process. In this work a porous mold insert with a regular deterministic geometry was developed and optimized through a numerical simulations to increase heat exchange between water and the cavity surface. An accurate mold numerical model was developed and experimentally validated. The results showed a substantial increase of the global coefficient of thermal conduction compared to the existing technologies for the rapid variation of the mold cavity temperature. A further experimental study was focused on the RHCM influence on microstructure and mechanical properties of long glass fibre reinforced polypropylene. X-ray computed tomography (CT) was employed to allow a direct observation of the fibres orientation and image analysis was used to measure the residual fibres length distribution. Tensile strength and fatigue analysis were performed in order to characterize the injection molded specimens, with a CIM and RHCM technologies, from static and dynamic point of view. The using of an high mold temperature resulted in a lower fibre orientation while the residual fibre length was enhanced. Concerning mechanical properties, the employment of a RHCM technology ensure an increasing of the tensile strength for thin wall components while both static and dynamic properties are decreased for thick parts. The mold temperature influence on injection molding of PET thin wall bottle preforms was also numerically investigated. The increasing in mold temperature resulted in a substantial decreasing of injection pressure without overcoming the limit of crystallization degree imposed by the subsequent blow molding process. A final aim of this work regarded the employment of a RHCM technology in order to control the mold temperature and the annealing phase during the injection molding of parts made with PLA. The analysis showed an interesting capability of adjusting the mold temperature in order to control the material crystallization degree and consequently its mechanical properties.

Abstract (italiano)

La tecnologia di riscaldamento e raffreddamento rapido dello stampo (RHCM) è ampliamente utilizzata per realizzare componenti senza difetti superficiali e con elevato gloss. Grazie ai numerosi vantaggi quali la riduzione della pressione di iniezione, l’aumento della qualità superficiale del componente stampato e la possibilità di controllare la temperatura stampo, questa tecnologia sta diventando una soluzione interessante per stampare parti in parete sottile. Tuttavia, la variazione di temperatura dello stampo aumenta sostanzialmente il tempo ciclo diminuendo la produttività. Sviluppare soluzioni e tecnologie per la variazione rapida della temperatura dello stampo è tecnicamente difficile a causa dei vincoli del processo di stampaggio ad iniezione. In questo lavoro è stato sviluppato uno stampo equipaggiato con inserti porosi di geometria definita per aumentare lo scambio termico tra l’acqua e la cavità stampo. A tal fine, un modello numerico accurato dello stampo è stato sviluppato e successivamente validato sperimentalmente. I risultati mostrano un sostanziale incremento del coefficiente globale di conduzione termica rispetto alle attuali tecnologie per la variazione rapida della temperatura stampo. Un ulteriore studio sperimentale fu focalizzato sull’influenza della tecnologia RHCM sulla microstruttura e sulle proprietà meccaniche di componenti stampati in polipropilene caricato con fibra lunga. Una tomografia computerizzata è stata utilizzata per consentire una diretta osservazione dell’orientazione delle fibre mentre una procedura innovativa è stata impiegata per misurare la lunghezza residua delle fibre. Analisi di trazione statica e di resistenza a fatica sono state svolte per caratterizzare i provini stampati con tecnologia convenzionale e con un processo RHCM. L’utilizzo di una elevata temperatura stampo risultò in una minore orientazione delle fibre mentre la lunghezza delle residua delle stesse fu incrementata. Per quanto riguarda le proprietà meccaniche, impiegare una tecnologia RHCM garantisce un aumento della resistenza a trazione per componenti a parete sottile, mentre sia le proprietà statiche che quelle dinamiche sono diminuite per parti di grosso spessore. L’influenza della temperatura stampo nello stampaggio ad iniezione di preforme a spessore sottile in PET è stata oltretutto investigata sperimentalmente. Un aumento della temperatura stampo risultò in una sostanziale diminuzione della pressione di iniezione senza superare il limite di cristallizzazione imposto dal sub-seguente processo di soffiaggio. Un ultimo scopo del lavoro riguarda l’utilizzo di una tecnologia RHCM per controllare la temperatura stampo ed il tempo di ricottura durante lo stampaggio ad iniezione di parti in PLA. L’analisi mostrò un’interessante dipendenza dalla temperatura stampo con il grado di cristallizzazione e conseguentemente con le proprietà meccaniche.

Statistiche Download - Aggiungi a RefWorks
Tipo di EPrint:Tesi di dottorato
Relatore:Lucchetta, Giovanni
Dottorato (corsi e scuole):Ciclo 28 > Scuole 28 > INGEGNERIA INDUSTRIALE > INGEGNERIA CHIMICA, DEI MATERIALI E MECCANICA
Data di deposito della tesi:26 Gennaio 2016
Anno di Pubblicazione:26 Gennaio 2016
Parole chiave (italiano / inglese):Rapid heat cycle molding; varioterm; fiber reinforced material; crystalline material
Settori scientifico-disciplinari MIUR:Area 09 - Ingegneria industriale e dell'informazione > ING-IND/16 Tecnologie e sistemi di lavorazione
Struttura di riferimento:Dipartimenti > Dipartimento di Ingegneria Industriale
Codice ID:9148
Depositato il:17 Ott 2016 12:12
Simple Metadata
Full Metadata
EndNote Format

Bibliografia

I riferimenti della bibliografia possono essere cercati con Cerca la citazione di AIRE, copiando il titolo dell'articolo (o del libro) e la rivista (se presente) nei campi appositi di "Cerca la Citazione di AIRE".
Le url contenute in alcuni riferimenti sono raggiungibili cliccando sul link alla fine della citazione (Vai!) e tramite Google (Ricerca con Google). Il risultato dipende dalla formattazione della citazione.

[ 1 ] G. Wang, G. Zhao, X. Wang, The International Journal of Advanced Manufacturing Technology 2013, 68, 1293 – 1310 . Cerca con Google

[ 2 ] G. Wang, G. Zhao, X. Wang, Materials & Design 2013, 44, 509 –520 . Cerca con Google

[ 3 ] G. Wang, G. Zhao, X. Wang, Materials & Design 2013, 46, 457 –472 . Cerca con Google

[ 4 ] M. Fiorotto, 2012. Cerca con Google

[ 5 ] G Lucchetta, M Fiorotto, P. Bariani, CIRP Annals-Manufacturing Technology 2012, 61, 539 – 542 . Cerca con Google

[ 6 ] F. Pisciotti, A. Boldizar, M. Rigdahl, I. Ariño, Polymer Engineering & Science 2005, 45, 1557 – 1567 . Cerca con Google

[ 7 ] E. Dawkins, K. Horton, P. Engelmann, Coloring Technology for Plastics 1999, 149 . Cerca con Google

[ 8 ] M. Oliveira, A. Brito, M. Costa, M. Costa, Polymer Engineering & Science 2006, 46, 1394 – 1401 . Cerca con Google

[ 9 ] X. Wang, G. Zhao, G. Wang, Materials & Design 2013, 47, 779 –792 . Cerca con Google

[ 10 ] B. H. Kim, R. R. Wadhwa, Polymer-Plastics Technology and Engineering 1987, 26, 1 – 22 . Cerca con Google

[ 11 ] D. Yao, S.-C. Chen, B. H. Kim, Advances in Polymer Technology 2008, 27, 233 – 255 . Cerca con Google

[ 12 ] K. Jansen, A. Flaman, Polymer Engineering & Science 1994, 34, 894 – 897 . Cerca con Google

[ 13 ] S.-C. Chen, W.-R. Jong, J.-A. Chang, Journal of Applied Polymer Science 2006, 101, 1174 – 1180 . Cerca con Google

[ 14 ] D. Yao, B. Kim, Polymer Engineering & Science 2002, 42, 2471 –2481 . Cerca con Google

[ 15 ] D. Yao, T. E. Kimerling, B. Kim, Polymer Engineering and Science 2006, 46, 938 . Cerca con Google

[ 16 ] R. X. Xu, E. Sachs, Polymer Engineering & Science 2009, 49, 305 –316 . Cerca con Google

[ 17 ] X. Xu, 1999. Cerca con Google

[ 18 ] K. Au, K. Yu, The International Journal of Advanced Manufacturing Technology 2007, 34, 496 – 515 . Cerca con Google

[ 19 ] D. Dimla, M Camilotto, F Miani, Journal of Materials Processing Technology 2005, 164, 1294 – 1300 . Cerca con Google

[ 20 ] S.-C. Chen, Y. Chang, T.-H. Chang, R.-D. Chien, International Communications in Heat and Mass Transfer 2008, 35, 130 – 138 . Cerca con Google

[ 21 ] M Smith, Z Guan, W. Cantwell, International Journal of Mechanical Sciences 2013, 67, 28 – 41 . Cerca con Google

[ 22 ] B. H. Kim, N. P. Suh, Polymer-Plastics Technology and Engineering 1986, 25, 73 – 93 . Cerca con Google

[ 23 ] M. J. Liou, N. P. Suh, Polymer Engineering & Science 1989, 29, 441 – 447 . Cerca con Google

[ 24 ] H Kataoka, H Yamaki, Y Umei, I Katou, JAPANESE JOURNAL OF POLYMER SCIENCE AND TECHNOLOGY 1998, 55, 671 –676 . Cerca con Google

[ 25 ] Y. Kim, K. Seong, S. Kang, Optical Engineering 2002, 41, 2276 –2281 . Cerca con Google

[ 26 ] J.-S. Lee, K.-W. Park, S.-W. Lee, J.-H. Kim, S. Kim, Optical Data Storage 2003, 228 – 30 . Cerca con Google

[ 27 ] K. Inoue, K. Hayashi, Y. Kawasaki, E. Ohno, Japanese journal of applied physics 2003, 42, 774 . Cerca con Google

[ 28 ] Y. Kim, J. Bae, H. Kim, S. Kang, Journal of Physics D: Applied Physics 2004, 37, 1319 . Cerca con Google

[ 29 ] D. Hatch, D. Kazmer, B. Fan, SPE ANTEC Tech. Papers 2001, 47, 428 – 432 . Cerca con Google

[ 30 ] W Schintlmeister, W Wallgram, J Kanz, K Gigl, Wear 1984, 100, 153 – 169 . Cerca con Google

[ 31 ] D. Yao, B. Kim, Applied thermal engineering 2003, 23, 341 – 352 . Cerca con Google

[ 32 ] S.-C. Chen, W.-R. Jong, Y.-J. Chang, J.-A. Chang, J.-C. Cin, Journal of Micromechanics and Microengineering 2006, 16, 1783 . Cerca con Google

[ 33 ] S. Kim, C.-S. Shiau, B. H. Kim, D. Yao, Polymer-Plastics Technology and Engineering 2007, 46, 1031 – 1037 . Cerca con Google

[ 34 ] K. Park, S. Choi, S.-J. Lee, Y.-S. Kim, Transactions of the KoreanSociety of Mechanical Engineers A 2008, 481 – 487 . Cerca con Google

[ 35 ] G. H. Brown, C. N. Hoyler, R. A. Bierwirth, et al., Theory and application of radio-frequency heating 1947. Cerca con Google

[ 36 ] L. Erwin, N. P. Suh, Polymer Engineering & Science 1976, 16, 841 – 846 . Cerca con Google

[ 37 ] S.-K. Byon, Apparatus for heating a mold for an injection molding system, US Patent 5 , 762 , 972 , 1998. Cerca con Google

[ 38 ] R. L. Akopyan, Dielectric mold for uniform heating and molding of polymers and composites in microwave ovens, US Patent 6 , 984 , 352 , 2006. Cerca con Google

[ 39 ] B. Whiteside, M. Martyn, P. Coates, P. Allan, P. Hornsby, G Greenway, Plastics rubber and composites 2003, 32, 231 – 239 . Cerca con Google

[ 40 ] S Kim, R Trichur, G Beaucage, C. Ahn, B. Kim in Proceedings of the 10 th solid-state sensor, actuator and microsystems workshop, 2002, pp. 206 – 209 . Cerca con Google

[ 41 ] Y Kurosaki, I Satoh, T Saito in Proceeding of the ASPE Spring Topical Meeting on Precision fabrication and Replication, Vol. 19, 1999, pp. 46 – 49 . Cerca con Google

[ 42 ] T. Saito, I. Satoh, Y. Kurosaki, Polymer Engineering & Science 2002, 42, 2418 – 2429 . Cerca con Google

[ 43 ] P.-C. Chang, S.-J. Hwang, Journal of applied polymer science 2006, 102, 3704 – 3713 . Cerca con Google

[ 44 ] P.-C. Chang, S.-J. Hwang, International Journal of Heat and Mass Transfer 2006, 49, 3846 – 3854 . Cerca con Google

[ 45 ] P. C. Chang, S. J. Hwang in Materials science forum, Vol. 505, Trans Tech Publ, 2006, pp. 1261 – 1266 . Cerca con Google

[ 46 ] M.-C. Yu, W.-B. Young, P.-M. Hsu, Materials Science and Engineering: A 2007, 460, 288 – 295 . Cerca con Google

[ 47 ] D. Yao, P. Nagarajan, L. Li, Y. Y. Allen, Journal of manufacturing science and engineering 2006, 128, 837 – 843 . Cerca con Google

[ 48 ] H. Stumpf, K. Schulte, Molds, cycle times, US Patent 5 , 824 , 237 , 1998. Cerca con Google

[ 49 ] N. Lee, J. Han, J. Lim, M. Choi, Y. Han, J. Hong, S. Kang, Japanese Journal of Applied Physics 2008, 47, 1803 . Cerca con Google

[ 50 ] H Iwami, M Fukuoka, Y Ohno, H Kanayama, H Hamada in ANTEC 2003 Conference Proceedings, 2003, pp. 468 – 472 . Cerca con Google

[ 51 ] C Kukla, H Loibl, H Detter, Kunststoffe-Plast Europe 1998, 88, 1331 – 1334 . Cerca con Google

[ 52 ] G. Zhao, G. Wang, Y. Guan, H. Li, Polymers for Advanced Technologies 2011, 22, 476 – 487 . Cerca con Google

[ 53 ] G. Wang, G. Zhao, H. Li, Y. Guan, Materials & Design 2010, 31, 382 – 395 . Cerca con Google

[ 54 ] W. Guilong, Z. Guoqun, L. Huiping, G. Yanjin, Materials & Design 2010, 31, 3426 – 3441 . Cerca con Google

[ 55 ] X.-P. Li, G.-Q. Zhao, Y.-J. Guan, M.-X. Ma, Materials & Design 2009, 30, 4317 – 4323 . Cerca con Google

[ 56 ] J. Thomason, M. Vlug, Composites Part A: Applied science and manufacturing 1996, 27, 477 – 484 . Cerca con Google

[ 57 ] J. Thomason, W. Groenewoud, Composites Part A: Applied Science and Manufacturing 1996, 27, 555 – 565 . Cerca con Google

[ 58 ] J. Thomason, M. Vlug, G Schipper, H. Krikor, Composites Part A: Applied Science and Manufacturing 1996, 27, 1075 – 1084 . Cerca con Google

[ 59 ] J. Thomason, M. Vlug, Composites Part A: Applied Science and Manufacturing 1997, 28, 277 – 288 . Cerca con Google

[ 60 ] J. Thomason, Composites Part A: Applied Science and Manufacturing 2002, 33, 1641 – 1652 . Cerca con Google

[ 61 ] J. Thomason, Composites Part A: Applied Science and Manufacturing 2005, 36, 995 – 1003 . Cerca con Google

[ 62 ] J. Thomason, Composites Part A: Applied Science and Manufacturing 2007, 38, 210 – 216 . Cerca con Google

[ 63 ] S Mukhopadhyay, B. Deopura, R Alagiruswamy, Journal of Thermoplastic Composite Materials 2003, 16, 479 – 495 . Cerca con Google

[ 64 ] J. Thomason, Composites Part A: Applied Science and Manufacturing 2002, 33, 1283 – 1288 . Cerca con Google

[ 65 ] K. S. Kumar, A. K. Ghosh, N. Bhatnagar, Polymer Composites 2007, 28, 259 – 266 . Cerca con Google

[ 66 ] R Bailey, H Kraft, International Polymer Processing 1987, 2, 94 –101 . Cerca con Google

[ 67 ] T. Vu-Khanh, J Denault, P Habib, A Low, Composites Science and Technology 1991, 40, 423 – 435 . Cerca con Google

[ 68 ] E. Lafranche, P. Krawczak, J.-P. Ciolczyk, J. Maugey, Advances in Polymer Technology 2005, 24, 114 – 131 . Cerca con Google

[ 69 ] H. Chen, M. Cieslinski, D. G. Baird in PROCEEDINGS OF PPS- 30 : The 30 th International Conference of the Polymer Processing Society–Conference Papers, Vol. 1664, AIP Publishing, 2014, pp. 478 – 482 . Cerca con Google

[ 70 ] D O’Regan, M Akay, Journal of materials processing technology 1996, 56, 282 – 291 . Cerca con Google

[ 71 ] J. Wang, C. Geng, F. Luo, Y. Liu, K. Wang, Q. Fu, B. He, Materials Science and Engineering: A 2011, 528, 3169 – 3176 . Cerca con Google

[ 72 ] T. Huan-Chang, C. Yuan-Jung, H. Chia-Hsiang, C. Rong-Yeu in PROCEEDINGS OF PPS- 30 : The 30 th International Conference of the Polymer Processing Society–Conference Papers, Vol. 1664, PPS Society, 2014, pp. 1149 – 1153 . Cerca con Google

[ 73 ] J. H. Phelps, A. I. A. El-Rahman, V. Kunc, C. L. Tucker, Composites Part A: Applied Science and Manufacturing 2013, 51, 11 –21 . Cerca con Google

[ 74 ] A. Durin, P. De Micheli, J. Ville, F. Inceoglu, R. Valette, B. Vergnes, Composites Part A: Applied Science and Manufacturing 2013, 48, 47 – 56 . Cerca con Google

[ 75 ] S. M. Dinh, R. C. Armstrong, Journal of Rheology (1978-present) 1984, 28, 207 – 227 . Cerca con Google

[ 76 ] V.-G. Gregorio M., T. I. Charles L. in PROCEEDINGS OF PPS-30 : The 30 th International Conference of the Polymer Processing Society–Conference Papers, Vol. 1664, PPS Society, 2014, pp. 609 – 613 . Cerca con Google

[ 77 ] K. J. Meyer, J. T. Hofmann, D. G. Baird, Composites Part A: Applied Science and Manufacturing 2014, 62, 77 – 86 . Cerca con Google

[ 78 ] T. B. N. Thi, M. Morioka, A. Yokoyama, S. Hamanaka, K. Yamashita, C. Nonomura in PROCEEDINGS OF PPS- 30 : The 30 th International Conference of the Polymer Processing Society–Conference Papers, Vol. 1664, AIP Publishing, 2015, p. 110011 . Cerca con Google

[ 79 ] P. Hine, B. Parveen, D. Brands, F. Caton-Rose, Composites Part A: Applied Science and Manufacturing 2014, 64, 70 – 78 . Cerca con Google

[ 80 ] G. B. Jeffery in Proceedings of the Royal Society of London A: Mathematical, Physical and Engineering Sciences, Vol. 102, The Royal Society, 1922, pp. 161 – 179 . Cerca con Google

[ 81 ] F. Folgar, C. L. Tucker, Journal of Reinforced Plastics and Composites 1984, 3, 98 – 119 . Cerca con Google

[ 82 ] J. Wang, J. F. O’Gara, C. L. Tucker III, Journal of Rheology (1978-present) 2008, 52, 1179 – 1200 . Cerca con Google

[ 83 ] J. H. Phelps, C. L. Tucker, Journal of Non-Newtonian Fluid Mechanics 2009, 156, 165 – 176 . Cerca con Google

[ 84 ] C. Hopmann, M Weber, J van Haag, M Schöngart in PROCEEDINGS OF PPS- 30 : The 30 th International Conference of the Polymer Processing Society–Conference Papers, Vol. 1664, AIP Publishing, 2015, p. 050008 . Cerca con Google

[ 85 ] R. Hertzberg, M. Skibo, J. Manson, Fatigue Mechanisms 1979, 471 . Cerca con Google

[ 86 ] S. Kultural, I. Eryurek, Materials & design 2007, 28, 816 – 823 . Cerca con Google

[ 87 ] A. Zago, G. S. Springer, Journal of reinforced plastics and composites 2001, 20, 564 – 595 . Cerca con Google

[ 88 ] A. Bernasconi, R. M. Kulin, Polymer Composites 2009, 30, 154 –161 . Cerca con Google

[ 89 ] S. Hitchen, S. Ogin, Composites science and technology 1993, 47, 239 – 244 . Cerca con Google

[ 90 ] J. Horst, J. Spoormaker, Polymer Engineering & Science 1996, 36, 2718 – 2726 . Cerca con Google

[ 91 ] J. Horst, J. Spoormaker, Journal of materials science 1997, 32, 3641 – 3651 . Cerca con Google

[ 92 ] A. B. C. Larbi, H Sidhom, K Sai, D Baptiste, Journal of materials engineering and performance 2006, 15, 575 – 580 . Cerca con Google

[ 93 ] L. Toubal, M. Karama, B. Lorrain, International journal of Fatigue 2006, 28, 1867 – 1872 . Cerca con Google

[ 94 ] H Nouri, F Meraghni, P Lory, International Journal of fatigue 2009, 31, 934 – 942 . Cerca con Google

[ 95 ] F Meraghni, H Nouri, N Bourgeois, C Czarnota, P Lory, Procedia Engineering 2011, 10, 2110 – 2116 . Cerca con Google

[ 96 ] F Meraghni, H Nouri, N Bourgeois, C Czarnota, P Lory, Procedia Engineering 2011, 10, 2110 – 2116 . Cerca con Google

[ 97 ] R Steinberger, T. V. Leitão, E Ladstätter, G Pinter, W Billinger, R. Lang, International Journal of Fatigue 2006, 28, 1340 – 1347 . Cerca con Google

[ 98 ] A Ghorbel, N Saintier, A Dhiab, Procedia Engineering 2011, 10, 2123 – 2128 . Cerca con Google

[ 99 ] B Esmaeillou, J Fitoussi, A Lucas, A Tcharkhtchi, Procedia Engineering 2011, 10, 2117 – 2122 . Cerca con Google

[ 100 ] B Esmaeillou, P Ferreira, V Bellenger, A Tcharkhtchi, Polymer Composites 2012, 33, 540 – 547 . Cerca con Google

[ 101 ] B Esmaeillou, P Fereirra, V Bellenger, A Tcharkhtchi, Journal of Applied Polymer Science 2012, 125, 4007 – 4014 . Cerca con Google

[ 102 ] J. Montesano, Z. Fawaz, H. Bougherara, Composite structures 2013, 97, 76 – 83 . Cerca con Google

[ 103 ] E Bayraktar, S Antolonovich, C Bathias, International Journal of Fatigue 2006, 28, 1322 – 1333 . Cerca con Google

[ 104 ] J Lambert, A. Chambers, I Sinclair, S. Spearing, Composites Science and Technology 2012, 72, 337 – 343 . Cerca con Google

[ 105 ] P. J. Withers, M. Preuss, Annual Review of Materials Research 2012, 42, 81 – 103 . Cerca con Google

[ 106 ] F Cosmi, A Bernasconi, Composites Science and Technology 2013, 79, 70 – 76 . Cerca con Google

[ 107 ] P. Mallick, Y. Zhou, International journal of fatigue 2004, 26, 941 – 946 . Cerca con Google

[ 108 ] A Bernasconi, P Davoli, A Basile, A Filippi, International Journal of Fatigue 2007, 29, 199 – 208 . Cerca con Google

[ 109 ] M.-H. R. Jen, C.-H. Lee, International Journal of Fatigue 1998, 20, 617 – 629 . Cerca con Google

[ 110 ] G Meneghetti, M Ricotta, G Lucchetta, S Carmignato, Composites Part B: Engineering 2014, 65, 17 – 25 . Cerca con Google

[ 111 ] F. Ellyin, Fatigue damage, crack growth and life prediction, Springer Science & Business Media, 2012. Cerca con Google

[ 112 ] G Meneghetti, International journal of fatigue 2007, 29, 81 – 94 . Cerca con Google

[ 113 ] G. Meneghetti, M. Quaresimin, Composites Part B: Engineering 2011, 42, 217 – 225 . Cerca con Google

[ 114 ] G. Tao, Z. Xia, International journal of fatigue 2007, 29, 2180 –2190 . Cerca con Google

[ 115 ] A Goel, K. Chawla, U. Vaidya, N Chawla, M Koopman, Materials characterization 2009, 60, 537 – 544 . Cerca con Google

[ 116 ] K. K. Chawla, Composite materials: science and engineering, Springer Science & Business Media, 2012. Cerca con Google

[ 117 ] M. F. Arif, N. Saintier, F. Meraghni, J. Fitoussi, Y. Chemisky, G. Robert, Composites Part B: Engineering 2014, 61, 55 – 65 . Cerca con Google

[ 118 ] M De Monte, E Moosbrugger, M. Quaresimin, Composites Part A: Applied Science and Manufacturing 2010, 41, 1368 – 1379 . Cerca con Google

[ 119 ] Y. Zhou, P. Mallick, Polymer composites 2006, 27, 230 – 237 . Cerca con Google

[ 120 ] P. Ladeveze, E LeDantec, Composites Science and Technology 1992, 43, 257 – 267 . Cerca con Google

[ 121 ] D Yao, B Kim in ANTEC 2003 Conference Proceedings, 2003, pp. 521 – 525 . Cerca con Google

[ 122 ] M. Song, Z Liu, M. Wang, T. Yu, D. Zhao, Journal of Materials Processing Technology 2007, 187, 668 – 671 . Cerca con Google

[ 123 ] M. Otsuka, A. Oyabe, H. Ito. Cerca con Google

[ 124 ] O. Brandau, Bottles, Preforms and Closures: A Design Guide for PET Packaging, William Andrew, 2012. Cerca con Google

[ 125 ] S. Meister, D. Drummer, The Scientific World Journal 2013, 2013. Cerca con Google

[ 126 ] D.-M. Fann, S. K. Huang, J.-Y. Lee, Polymer Engineering & Science 1998, 38, 265 – 273 . Cerca con Google

[ 127 ] R Zheng, P. Kennedy, Journal of Rheology (1978-present) 2004, 48, 823 – 842 . Cerca con Google

[ 128 ] J. C. Viana, N. M. Alves, J. F. Mano, Polymer Engineering & Science 2004, 44, 2174 – 2184 . Cerca con Google

[ 129 ] H. Liu, J. Zhang, Journal of polymer science part B: Polymer Physics 2011, 49, 1051 – 1083 . Cerca con Google

[ 130 ] A. P. Mathew, K. Oksman, M. Sain, Journal of Applied Polymer Science 2006, 101, 300 – 310 . Cerca con Google

[ 131 ] Q Zhou, M Xanthos, Polymer degradation and stability 2008, 93, 1450 – 1459 . Cerca con Google

[ 132 ] A. M. Harris, E. C. Lee, Journal of applied polymer science 2008, 107, 2246 – 2255 . Cerca con Google

[ 133 ] Y. Srithep, P. Nealey, L.-S. Turng, Polymer Engineering & Science 2013, 53, 580 – 588 . Cerca con Google

[ 134 ] M. Panigrahi, N. K. Singh, R. K. Gautam, R. M. Banik, P. Maiti, Composite Interfaces 2010, 17, 143 – 158 . Cerca con Google

[ 135 ] G. Kfoury, J.-M. Raquez, F. Hassouna, J. Odent, V. Toniazzo, D. Ruch, P. Dubois, Frontiers in chemistry 2013, 1. Cerca con Google

[ 136 ] K. Zhang, V. Nagarajan, M. Misra, A. K. Mohanty, ACS applied materials & interfaces 2014, 6, 12436 – 12448 . Cerca con Google

[ 137 ] K. Zhang, A. K. Mohanty, M. Misra, ACS applied materials & interfaces 2012, 4, 3091 – 3101 . Cerca con Google

[ 138 ] S. Saeidlou, M. A. Huneault, H. Li, C. B. Park, Journal of Applied Polymer Science 2014, 131. Cerca con Google

[ 139 ] Y. Srithep, P. Nealey, L.-S. Turng, Polymer Engineering & Science 2013, 53, 580 – 588 . Cerca con Google

[ 140 ] V. Nagarajan, K. Zhang, M. Misra, A. K. Mohanty, ACS applied materials & interfaces 2015. Cerca con Google

[ 141 ] B Suksut, C Deeprasertkul, Journal of Polymers and the Environment 2011, 19, 288 – 296 . Cerca con Google

[ 142 ] B Suksut, C Deeprasertkul, Journal of Polymers and the Environment 2011, 19, 288 – 296 . Cerca con Google

[ 143 ] A. K. Bledzki, A. Jaszkiewicz, D. Scherzer, Composites Part A: Applied science and manufacturing 2009, 40, 404 – 412 . Cerca con Google

[ 144 ] M. Huda, L. Drzal, A. Mohanty, M Misra, Composites Part B: Engineering 2007, 38, 367 – 379 . Cerca con Google

[ 145 ] L. Suryanegara, A. N. Nakagaito, H. Yano, Cellulose 2010, 17, 771 – 778 . Cerca con Google

[ 146 ] S. Molinaro, M. C. Romero, M. Boaro, A. Sensidoni, C. Lagazio, M. Morris, J. Kerry, Journal of Food Engineering 2013, 117, 113 –123 . Cerca con Google

[ 147 ] N Najafi, M. Heuzey, P. Carreau, Polymer Engineering & Science 2013, 53, 1053 – 1064 . Cerca con Google

[ 148 ] G. Ryan, P. McGarry, A. Pandit, D. Apatsidis, Journal of Biomedical Materials Research Part B: Applied Biomaterials 2009, 90, 894 –906 . Cerca con Google

[ 149 ] M Vesenjak, C Veyhl, T Fiedler, Materials Science and Engineering: A 2012, 541, 105 – 109 . Cerca con Google

[ 150 ] J.-P. Kruth, M Bartscher, S Carmignato, R Schmitt, L. De Chiffre, A Weckenmann, CIRP Annals-Manufacturing Technology 2011, 60, 821 – 842 . Cerca con Google

[ 151 ] L. De Chiffre, S Carmignato, J.-P. Kruth, R Schmitt, A Weckenmann, CIRP Annals-Manufacturing Technology 2014, 63, 655 –677 . Cerca con Google

[ 152 ] M Berton, A Cellere, G Lucchetta, International Journal of Material Forming 2010, 3, 671 – 674 . Cerca con Google

[ 153 ] A. Huq, J Azaiez, Polymer Engineering & Science 2005, 45, 1357 –1368 . Cerca con Google

[ 154 ] S. G. Advani, C. L. Tucker III, Journal of Rheology (1978-present) 1987, 31, 751 – 784 . Cerca con Google

[ 155 ] P. C. Painter, M. M. Coleman, Fundamentals of polymer science: an introductory text, Technomic Lancaster, PA, 1997. Cerca con Google

[ 156 ] T. A. Osswald, Understanding polymer processing: processes and governing equations, Hanser, 2011. Cerca con Google

[ 157 ] I. Arino, U. Kleist, L. Mattsson, M. Rigdahl, Polymer Engineering & Science 2005, 45, 1343 – 1356 . Cerca con Google

[ 158 ] I. Arino, U. Kleist, M. Rigdahl, Polymer Engineering & Science 2005, 45, 733 – 744 . Cerca con Google

[ 159 ] F. B. Leloup, G. Obein, M. R. Pointer, P. Hanselaer, Color Research & Application 2014, 39, 559 – 570 . Cerca con Google

[ 160 ] R. S. Hunter, METHODS 1937. Cerca con Google

[ 161 ] S.-C. Chen, P. S. Minh, J.-A. Chang, S.-W. Huang, C.-H. Huang, International Communications in Heat and Mass Transfer 2012, 39, 216 – 223 . Cerca con Google

[ 162 ] A. Agazzi, V. Sobotka, R. LeGoff, Y. Jarny, Applied Thermal Engineering 2013, 52, 170 – 178 . Cerca con Google

[ 163 ] G. Wang, G. Zhao, H. Li, Y. Guan, Expert Systems with Applications 2011, 38, 6705 – 6719 . Cerca con Google

[ 164 ] H. HT., Fatigue of composites, Delware Composites Design Encyclopedia, 1990. Cerca con Google

[ 165 ] P.-A. Eriksson, A.-C. Albertsson, P Boydell, K Eriksson, J.-A. Månson, Polymer composites 1996, 17, 823 – 829 . Cerca con Google

[ 166 ] P.-A. Eriksson, A.-C. Albertsson, P Boydell, G Prautzsch, J.-A. Månson, Polymer composites 1996, 17, 830 – 839 . Cerca con Google

[ 167 ] S.-Y. Fu, B Lauke, E Mäder, C.-Y. Yue, X Hu, Composites Part A: Applied Science and Manufacturing 2000, 31, 1117 – 1125 . Cerca con Google

[ 168 ] S. Hitchen, S. Ogin, P. Smith, Composites 1995, 26, 303 – 308 . Cerca con Google

[ 169 ] H. Huang, R. Talreja, Composites science and technology 2006, 66, 2743 – 2757 . Cerca con Google

[ 170 ] P. Mallick, Y. Zhou, International journal of fatigue 2004, 26, 941 – 946 . Cerca con Google

[ 171 ] W. B. Nelson, Accelerated testing: statistical models, test plans, and data analysis, Vol. 344, John Wiley & Sons, 2009. Cerca con Google

[ 172 ] V. Azzi, S. Tsai, Experimental mechanics 1965, 5, 283 – 288 . Cerca con Google

[ 173 ] F Ellyin, H El-Kadi, Composite Structures 1990, 15, 61 – 74 . Cerca con Google

[ 174 ] I. Carrascal, J. Casado, S Diego, J. Polanco, F GUTIÉRREZ-SOLANA, Fatigue & Fracture of Engineering Materials & Structures 2012, 35, 683 – 691 . Cerca con Google

[ 175 ] N. G. McCrum, C. Buckley, C. B. Bucknall, Principles of polymer engineering, Oxford University Press, 1997. Cerca con Google

[ 176 ] N Chawla, C Andres, J. Jones, J. Allison, Scripta materialia 1998, 38, 1595 – 1600 . Cerca con Google

[ 177 ] B Mlekusch, Composites Science and Technology 1999, 59, 547 –560 . Cerca con Google

[ 178 ] C. Eberhardt, A. Clarke, Composites Science and Technology 2001, 61, 1389 – 1400 . Cerca con Google

[ 179 ] Y. Lee, S. Lee, J. Youn, K. Chung, T. Kang, Materials Research Innovations 2002, 6, 65 – 72 . Cerca con Google

[ 180 ] S.-Y. Fu, Y.-W. Mai, E. C.-Y. Ching, R. K. Li, Composites Part A: Applied Science and Manufacturing 2002, 33, 1549 – 1555 Cerca con Google

Download statistics

Solo per lo Staff dell Archivio: Modifica questo record